Method for producing pad conditioner for semiconductor substrates
AssigneeNippon Steel Corporation
InventorsToshiya Kinoshita, Motonori Tamura
Life of this patent
Estimating the term…
Abstract
A pad conditioner for semiconductor substrates for performing conditioning by slide contact with the abrasive surface of the polishing pad comprises a support member having a surface opposed to the polishing pad, a joining alloy layer covering the above surface of the support member, and a group of hard abrasive grains which are spread out and embedded in the joining alloy layer and supported by the joining alloy layer. At the contact interface between each of the hard abrasive grains and the above joining alloy, the surfaces of the hard abrasive grains are covered with either a layer of metallic carbides or a layer of metallic nitrides. Ag-base and Ag—Cu-base alloys, etc., can be used as the joining alloys.
Claims12
A method of producing a pad conditioner for a polishing pad for semiconductor substrates for performing conditioning by bringing the conditioner into slide-contact with the polishing surface of the polishing pad, which comprises the steps of:
- preparing a support member having a surface opposed to said polishing pad, a joining alloy material comprising an active metal, and a powder of hard abrasive grains;
- forming a layer of said joining alloy material on the surface of said support member opposed to said polishing pad;
- putting said powder of hard abrasive grains on the surface of said joining alloy material layer so as to uniformly distribute;
- inserting said support member to which said joining alloy material and said powder of hard abrasive grains are applied into a vacuum heating furnace;
- degassing said vacuum heating furnace to vacuum;
- raising the furnace temperature to the range of 650° C. to 1200° C. and holding it for a predetermined time to cause said respective hard abrasive grains to partially enter into said joining alloy material layer in a molten state;
- and
- lowering the furnace temperature to room temperature.
A method of producing a pad conditioner for semiconductor substrates for performing conditioning by bringing the conditioner into slide-contact with the polishing surface of the polishing pad, comprising the steps of:
- preparing a support member having a surface opposed to said polishing pad, and a joining alloy material;
- preparing a powder composed of hard abrasive grains in which any one of the films selected from the group consisting of an active metal film, a film of an active-metal carbide, and a film of an active-metal nitride is applied to the surface of each grain;
- forming a layer of said joining alloy material on the above surface of said support member opposed to said polishing pad;
- putting said powder of hard abrasive grains on the surface of said joining alloy material layer so as to uniformly distribute;
- inserting said support member to which said joining alloy material and said powder of hard abrasive grains are applied into a vacuum heating furnace;
- degassing said vacuum heating furnace to vacuum;
- raising the furnace temperature to the range of 650° C. to 1200° C. and holding it for a predetermined time;
- causing said respective hard abrasive grains to partially enter into said joining alloy material layer in a molten state;
- and
- lowering the furnace temperature to room temperature.