Process for polymerization of olefins

A process for the polymerization of olefins, which comprises polymerizing an olefin or mixture thereof in presence of a solvent, a supported metallocene and an aluminoxane as cocatalyst in a hydrocarbon medium, at a temperature in the range of 50 to 150° C., at a pressure ranging between 1 to 20 bar, for a period of 10 minutes to 10 hours, scavenging the reaction mixture by addition of an organoaluminum compound to remove the last traces of impurities of solvent, separating the polymer by washing the polymer with an organic solvent, drying the polymer to remove the solvent to obtain the product;

• wherein the supported metallocene has a central metal chosen from groups IIIB, IVB, VB, and VIB of the Periodic Table;
• and wherein the supported metallocene catalyst for the polymerization of the olefins is prepared by a process comprising preparing a precursor catalyst material, by preparing a solution (A) of a magnesium halide in an electron donor solvent in which the magnesium halide is completely soluble;
• heating the solution (A) to a temperature in the range of 20° C. to the boiling point of the electron donor solvent for a period ranging between 10 to 60 minutes;
• separately preparing a solution (B) of a metallocene compound in the same electron donor solvent, heating the solution (B) to a temperature in the range of 25° C. to 70° C. for a period ranging between 0.1 to 0.5 hrs., mixing the two solutions (A) and (B) to obtain a homogenous solution of catalyst precursor compound;
• stirring and maintaining a resulting homogenous solution at a temperature in the range of 50° C. to 70° C. for a period of 0.5 to 2 hrs.;
• separately preparing a slurry of a support in a liquid hydrocarbon medium;
• heating the slurry to a temperature in the range of 50° C. to 75° C. and stirring for a period of 0.25 to 2 hrs.;
• mixing the homogenous solution of the catalyst precursor compound with the resulting slurry of the support to produce a product slurry, stirring the product slurry for 0.5 to 3 hrs at a temperature ranging between 50° C. to 70° C.;
• cooling the product slurry to room temperature under an inert atmosphere;
• separating the resulting solid supported metallocene catalyst from the solvents of the product slurry, washing the solid supported metallocene catalyst with a hydrocarbon solvent, and drying the catalyst under vacuum.