Barium titanate-based semiconductive ceramic composition

Abstract

A barium titanate-based semiconductive ceramic composition for facilitating miniaturization of thermistor devices by improving rush current resistance characteristics is provided. In the barium titanate-based semiconductive ceramic composition, a fraction of the Ba in BaTiO3 as the major component is replaced with 1 to 25 mole percent of Ca, 1 to 30 mole percent of Sr, and 1 to 50 mole percent of Pb; and wherein to 100 mole percent of the major component, the semiconductivity-imparting agent is added in an amount of 0.2 to 1.0 mole percent as a converted element content, and the additive comprises manganese oxide in an amount of 0.01 to 0.10 mole percent as a converted Mn content, silica in an amount of 0.5 to 5 mole percent as a converted SiO2 content, and magnesium oxide in an amount of 0.028 to 0.093 mole percent as a converted Mg content.