US 6,187,706 B1 · Silicon nitride sintered body and method of producing the same

Abstract

There is disclosed a silicon nitride sintered body produced by sintering a molded article which comprises a mixture of a silicon nitride powder as the main component and plural kinds of sintering additives, wherein said silicon nitride powder is set to be 0.1 to 1.0 μm in average grain size, and said plural kinds of sintering additives includes first and second sintering additives, said first sintering additive comprising oxide powders of at least one element of Group 3a element, said second sintering additive comprising oxide powders of at least one element selected from Zr (zirconium), Hf (hafnium), Nb (niobium), Ta (tantalum) and W (tungsten), said first sintering additive having the average grain size set to be 0.1 to 10 times as large as the average grain size of said silicon nitride powder and being incorporated in an amount ranging from 0.1 to 10% by weight to the mixture, said second sintering additive being such particles as that part of the particles are of grain size in the range from 10 to 100 times as large as the average grain size of said silicon nitride powder but the number of such part of the particles is in the 5 to 50% range of the total particle number and being incorporated in an amount ranging from 0 to 10% by weight to the mixture (provided that 0% by weight is not included). The sintering process of the molded article comprises a primary sintering in an atmosphere containing a nitrogen gas under the atmospheric pressure from 1 to 20 kgf/cm2 at 1600-1800° C., and subsequently secondary sintering in an atmosphere containing a nitrogen gas under the atmospheric pressure ranging from 100 to 2000 kgf/cm2 at a temperature lower than that of primary sintering.

Claims8

Dependent claims

A method of producing a silicon nitride sintered body by molding a starting material comprising sintering additives and a silicon nitride powder to form a molded article and subjecting the molded article to a primary sintering and a secondary sintering in a nitrogen atmosphere, wherein the primary sintering and the secondary sintering are carried out under the following conditions:

a first temperature of said primary sintering being higher than a grain boundary temperature that a grain boundary phase is crystallized for said starting material and not more than 100° C. higher than said grain boundary temperature;
said primary sintering being up to 6 hours longer than a point in time at which a contraction has started as a dense β silicon nitride is formed during said primary sintering;
said primary sintering being at a pressure of 0.1 kgf/.cm2˜3.0 kgf/cm2;
a second temperature of said secondary sintering being higher than said grain boundary temperature at which the grain boundary phase is crystallized but lower than said first temperature of primary sintering for promoting the crystallinity of the grain boundary phase and preventing abnormal grain growth;
and
said secondary sintering being at a pressure of 100 kgf/cm2˜2000 kgf/cm2;
wherein said grain boundary temperature at which the grain boundary phase is crystallized is determined by selecting a temperature at which a crystallinity of said grain boundary phase is the highest among a plurality of molded articles prepared from the starting material and sintered at different temperatures;
and said contraction starting point time as said dense β silicon nitride is formed is determined from the relation between a progress time and a contraction ratio at the time of being heated at said primary sintering first temperature.

5 more elements

A method of producing a silicon nitride sintered body by the steps of:

molding a molded article of a starting material which comprises a mixture of a silicon nitride powder as a main component and plural sintering additives, said silicon nitride powder being 0.1 to 1.0 μm in average grain size, and said plural sintering additives include first and second sintering additives, said first sintering additive comprising oxide powders of at least one element of Group 3a elements, said second sintering additive comprising oxide powders of at least one element selected from Hf (hafnium), Nb (niobium), Ta (tantalum) and W (tungsten), said first sintering additive having an average grain size of 0.1 to 10 times as large as the average grain size of said silicon nitride powder and being incorporated in an amount ranging from 0.1 to 10% by weight of the mixture, said second sintering additive being particles and a part of the particles being of a grain size in the range from 15 to 50 times as large as the average grain size of said silicon nitride powder with a number of said part of said second sintering additive particles of said grain size being in a 5 to 50% range of a total number of particles of said second sintering additive, and said second sintering additive being incorporated in an amount ranging from greater than 0 to 10% by weight of the mixture;
and
sintering said molded article.

Dependencies are inferred from the claim text.

Silicon nitride sintered body and method of producing the same

Life of this patent

Silicon nitride sintered body and method of producing the same

Life of this patent

Abstract

Claims8