Process for preparing silica gel and process for producing dehumidifying element
AssigneeNichias Corporation
InventorsJun Tanabe, Yumiko Furuya
Life of this patent
Estimating the term…
Abstract
A process for preparing silica gel is disclosed. The silica gel is produced by immersing a base in silica sol, drying the impregnated base in a mixed solution of an alkali silicate and an alkali hydroxide, removing the impregnated base form the mixed solution, heating the impregnated base, and subsequently treating the impregnated base with an acid. A sufficient amount of silica gel for use as a dehumidifying element can be produced through a single series of treatments.
Claims3
A process for preparing a fibrous structure suitable for use as a dehumidification element impregnated with at least about 80 kg/m3 of silica gel, comprising:
- initially immersing a fibrous structure in silica sol to form an impregnated structure,
- drying the resulting impregnated structure,
- immersing the dried impregnated structure in a mixed solution of an alkali silicate solution and an alkali hydroxide solution, said alkali silicate solution having an alkali silicate content of 20 to 35 wt % and said alkali hydroxide solution having an alkali hydroxide content of 20 to 50 wt %, wherein the molar ratio of silicon oxide to alkali oxide is adjusted so that it does not exceed 10,
- removing the impregnated structure from the mixed solution,
- heating the impregnated structure removed from the mixed solution at from 30-90° C. for at least 15 minutes, and thereafter
- treating the resulting structure with an aqueous acid solution, and
- subsequently drying the thus treated structure.
A process for producing a honeycomb fibrous structure dehumidifying element impregnated with a least about 80 Kg/m3 of silica gel, comprising:
- processing inorganic fiber paper into a honeycomb structure,
- initially immersing the honeycomb structure in silica sol, to form an impregnated honeycomb structure,
- drying the resulting impregnated honeycomb structure,
- immersing the dried impregnated honeycomb structure in a mixed solution of an alkali silicate solution and an alkali hydroxide solution, said alkali silicate solution having an alkali silicate content of 20 to 35 wt % and said alkali hydroxide solution having an alkali hydroxide content of 20 to 50 wt %, wherein the ratio of silicon oxide to alkali oxide is adjusted so that it does not exceed 10,
- removing the impregnated honeycomb structure from the mixed solution,
- heating the impregnated honeycomb structure removed from the mixed solution at from 30-90° C. for at least 15 minutes, and thereafter
- treating the resulting honeycomb structure with an aqueous acid solution, and
- subsequently drying the thus treated honeycomb structure.
A process for producing a dehumidifying element impregnated with a least about 80 Kg/m3 of silica gel, comprising:
- initially immersing inorganic fiber paper in silica sol, to form an impregnated inorganic fiber paper,
- drying the resulting impregnated inorganic fiber paper,
- immersing the dried impregnated inorganic fiber paper in a mixed solution of an alkali silicate solution and an alkali hydroxide solution, said alkali silicate solution having an alkali silicate content of 20 to 35 wt % and said alkali hydroxide solution having an alkali hydroxide content of 20 to 50 wt %, wherein the molar ratio of silicon oxide to alkali oxide is adjusted so it does not exceed 10,
- removing the impregnated inorganic fiber paper from the mixed solution,
- processing the resulting impregnated inorganic fiber paper removed from the mixed solution into a honeycomb structure,
- heating the honeycomb structure at from 30-90° C. for at least 15 minutes, and thereafter
- treating the resulting honeycomb structure with an aqueous acid solution, and
- subsequently drying the thus treated honeycomb structure.
Dependencies are inferred from the claim text.