Wound dressing material containing silk fibroin and sericin as main component and method for preparing same

A wound dressing material which comprises a dense and non-porous film of crystallinity below 10%, the film containing 0 to 99% by weight of fibroin and 1 to 100% by weight of sericin and having density of 1.1 to 1.4 g/cm3, thickness of 10 to 130 μm, water absorption of 100% or more after one hour-immersion in water at room temperature and a water soluble portion in an amount of 10% or more.

A method for preparing a wound dressing material comprising an amorphous film of crystallinity below 10% and containing fibroin and sericin as a main component which comprises dissolving a raw material selected from the group consisting of cocoonfilaments, raw silk, silk fabrics, silk yarn or unscoured materials thereof, or obtained by mixing independently separated and prepared fibroin and sericin to said raw material in an aqueous solution of a neutral salt, demineralizing the neutral salt in the aqueous solution through dialysis to form a fibroin-sericin containing aqueous solution, removing insolubles from the aqueous solution by filtration or centrifugation, and then casting the aqueous solution on a smooth solid surface, followed by drying.

A method for preparing a wound dressing material comprising an amorphous film of crystallinity below 10% and containing fibroin and sericin as a main component which comprises mixing an aqueous fibroin solution and an aqueous sericin solution, demineralizing and drying.

A method for preparing a wound dressing material comprising an amorphous film of crystallinity below 10% and containing fibroin and sericin as a main component which comprises adding fibers, powders or films which contain sericin and fibroin to a solution formed by mixing an aqueous solution of fibroin and an aqueous solution of sericin, dissolving these fibers, powders or films by adding a neutral salt, demineralizing the neutral salt in the aqueous solution through dialysis to form an aqueous solution containing fibroin and sericin, removing insolubles from the aqueous solution, then casting the aqueous solution on a smooth solid surface, followed by drying.

A method for preparing a wound dressing material comprising an amorphous film of crystallinity below 10% and containing fibroin and sericin as a main component which comprises dissolving fibroin and sericin obtained by independent separation and formed from a raw material selected from a group consisting of cocoon filaments, raw silk, silk fabrics or unscoured materials thereof in the presence of a neutral salt, demineralizing, casting an aqueous solution containing fibroin and sericin on a smooth solid surface, followed by drying.

A powder type wound dressing material which comprises fibroin and sericin as a main component.

A method for preparing a powder type wound dressing material containing fibroin and sericin as a main component which comprises dissolving a raw material selected from the group consisting of cocoonfilaments, raw silk, silk fabrics silk yarn or unscoured materials thereof containing protein fiber-originated fibroin and sericin as a silkworm product, or obtained by mixing independently separated and prepared fibroin and sericin to said raw material in an aqueous solution of a neutral salt, demineralizing the neutral salt in the aqueous solution through dialysis to form a fibroin-sericin containing aqueous solution, removing insolubles from the aqueous solution by filtration or centrifugation, and then casting the aqueous solution on a smooth solid surface, drying and pulverizing the thus obtained amorphous film of crystallinity below 10% which contains fibroin and sericin as a main component.

A method for preparing a powder type wound dressing material containing fibroin and sericin as a main component which comprises dissolving fibroin or sericin, which is separated and obtained from a raw material selected from a group consisting of cocoonfilaments, raw silk, silk fabrics silk yarn or unscoured materials thereof containing protein fiber-originated fibroin and sericin as a silkworm product, in an aqueous medium in the presence of a neutral salt, demineralizing the neutral salt in the aqueous solution through dialysis to form a fibroin-sericin containing aqueous solution, removing insolubles from the aqueous solution by filtration or centrifugation, and then casting the aqueous solution on a smooth solid surface, drying and pulverizing the thus obtained amorphous film of crystallinity below 10% which contains fibroin and sericin as a main component.

A method for preparing a powder type wound dressing material containing fibroin and sericin as a main component which comprises mixing fibroin and sericin in a state of solution, demineralizing, drying and pulverizing the thus obtained amorphous film of crystallinity below 10% which contains fibroin and sericin as a main component.

A method for preparing a powder type wound dressing material containing fibroin and sericin as a main component which comprises adding fibers, powder and film of sericin or fibroin to fibroin or sericin in a state of solution, demineralizing, drying and pulverizing the thus obtained amorphous film of crystallinity below 10% which contains fibroin and sericin as a main component.