Thermostable polymer electrolyte gel

Abstract

A thermostable polymer electrolyte gel containing an acrylonitrile polymer, an electrolyte and a solvent, the acrylonitrile polymer having an acrylonitrile content of from 89 wt % to 98 wt % and meeting the following relationship: 1,040,000-(A.times.10,000).ltoreq.B.ltoreq.1,490,000-(A.times.10,000) where A is the acrylonitrile content in wt % and B is the weight average molecular weight of the acrylonitrile polymer, the polymer electrolyte gel having an ion conductivity of 10.sup.-3 S/cm or higher at 20.degree. C., exhibiting the "retention of shape" in a thermostability test, and containing the acrylonitrile polymer in a proportion of from 3 wt % to 9 wt %. The thermostable polymer electrolyte gel can be produced by dissolving an acrylonitrile polymer and an electrolyte in a solvent to prepare a solution of the polymer, and cooling the polymer solution to a temperature of 0.degree. C. or lower.