Back to results
US 6,149,847 AGranted
Method of and apparatus for the production of polyester yarn
AssigneeKrupp Uhde GmbH
InventorsRudolf Geier, Ingo Efflander, Jurgen Hartig
Life of this patent
Estimating the term…
Abstract
Polyester yarn is made by melt spinning the polyester filaments which are then cooled at least to solidification and heated by counterflow with prestretching to a crystallinity in excess of 24%. The prestretched filaments are gathered and stretched to after-stretching at a temperature of 80.degree. C. to 250.degree. C. to a final titer of 1.0 dtex to 7.5 dtex with a stretching ratio of 1:1.5 to 1:1.15. The yarn is then wound up at a rate of 5000 to 8000 m/min.
Claims7
A method of making a polyester yarn, comprising the steps of:
- (a) melt-spinning a multiplicity of molten polyester filaments;
- (b) cooling said molten polyester filaments at least sufficiently to solidify them into solid polyester filaments;
- (c) heating and prestretching said solid polyester filaments by passing said solid polyester filaments separated from one another through a counterflow heating zone in counterflow to a gaseous medium while heating said solid polyester filaments to a temperature of 100.degree. C. to 199.degree. C. and above the glass transition temperature thereof to generate a crystallinity of >24% in prestretched polyester filaments;
- (d) thereafter gathering the prestretched polyester filaments and stretching the gathered polyester filaments as a yarn to a final titer following the stretching of 1.0 dtex to 7.5 dtex at a temperature of 80.degree. C. to 250.degree. C. and at a stretching ratio of 1:1.5 to 1:1.15;
- and
- (e) thereafter winding up said yarn at a rate of 5000 m/min to 8000 m/min.
3 more elements
An apparatus for making a polyester yarn comprising:
- a spinneret for melt spinning a multiplicity of molten polyester filaments;
- a cooling station downstream of said spinneret for cooling said molten polyester filaments at least sufficiently to solidify them into solid polyester filaments;
- means downstream of said cooling station for heating and prestretching said solid polyester filaments by passing said solid polyester filaments separated from one another through a counter-flow heating zone in a counterflow to a gaseous medium in an amount of 5 m.sup.3 /h to 50 m.sup.3 /h while heating said solid polyester filaments to a temperature of 100.degree. C. to 199.degree. C. and above the glass transition temperature thereof to generate a crystallinity greater than about 24% in prestretched polyester filaments;
- means for gathering the prestretched polyester filaments into a yarn and stretching the yarn to a final titer of 1.0 dtex to 7.5 dtex at a temperature of 80.degree. C. to 250.degree. C. at a stretched ratio of 1:1.5 to 1:1.15;
- and
- means for winding up the stretched yarn at a rate of 5000 m/min to 8000 m/min.
- a spinneret for melt spinning a multiplicity of molten polyester filaments;
- a cooling station downstream of said spinneret for cooling said molten polyester filaments at least sufficiently to solidify them into solid polyester filaments;
- means downstream of said cooling station for heating and prestretching said solid polyester filaments by passing said solid polyester filaments separated from one another through a counterflow heating zone in a counterflow to a gaseous medium in an amount of 5 m.sup.3 /h to 50 m.sup.3 /h while heating said solid polyester filaments to a temperature of 100.degree. C. to 199.degree. C. and above the blast transition temperature thereof to generate a crystallinity greater than about 24% in prestretched polyester filaments;
- means for gathering the prestretched polyester filaments into a yarn and stretching the yarn to a final titer of 1.0 dtex to 7.5 dtex at a temperature of 80.degree. C. to 250.degree. C. at a stretched ratio of 1:1.5 to 1:1.15;
- and
- means for winding up the stretched yarn at a rate of 5000 m/min to 8000 m/min.
9 more elements
Dependencies are inferred from the claim text.