Process for producing polyethylene film composition having broad molecular weight distribution and improved bubble stability

Abstract

A process for producing a polyethylene film composition, comprising melt extruding a linear copolymer of ethylene and at least one other olefin having from 3 to 8 carbon atoms, said linear copolymer having a bimodal distribution comprising a high molecular weight fraction having a weight average molecular weight of at least 600,000 and a low molecular weight fraction having a weight average molecular weight of less than 20,000 at a temperature of from 195 to 285.degree. C. in the presence of oxygen in an amount of from about 0.5 to about 6% by volume to improve bubble stability without any significant reduction in tear strength of film produced from said melt extruded linear copolymer.

Dependencies are inferred from the claim text.