Composite capacitor electrode for a DRAM cell
AssigneeTaiwan Semiconductor Manufacturing Company, Ltd.
InventorsShau-Lin Shue, Cheng-Yeh Shih
Life of this patent
Estimating the term…
Abstract
A process for creating a storage node electrode, for a DRAM cell, exhibiting increased surface area resulting from the formation of an agglomerated metal silicide layer, on the top surface of the storage node electrode, has been developed. The process features creating a polysilicon, storage node electrode shape, followed by the formation of an overlying, agglomerated titanium disilicide layer. The agglomerated titanium disilicide layer is formed from a RTA procedure, applied to a smooth titanium disilicide layer, located on the polysilicon, storage node electrode.
Claims18
A method for fabricating a two layer, storage node electrode, for a DRAM device, on a semiconductor substrate, comprising the steps of:
- providing a transfer gate transistor, on said semiconductor substrate;
- forming a conductive plug, in a storage node contact hole, in an insulator layer, with said conductive plug contacting underlying source/drain region, of said underlying transfer gate transistor;
- forming a storage node electrode shape, comprised of a first conductive layer, with a first portion of said storage node electrode shape contacting underlying conductive plug, and with a second portion of said storage node shape overlying a portion of the top surface of said insulator layer;
- depositing a metal layer;
- performing a first anneal procedure to form a smooth first metal silicide layer, at a temperature of 750.degree. C., or less, on all surfaces of said first conductive layer, located only on all surfaces of said storage node electrode shape, leaving a portion of said metal layer, overlying a portion of the top surface of said insulator layer, unreacted;
- selectively removing portion of said unreacted metal layer;
- performing a second anneal procedure, at a temperature between about 800 to 1000.degree. C., to convert said smooth first metal silicide layer to a agglomerated, second metal silicide layer, on said first conductive layer, of said storage node electrode shape, resulting in said two layer, storage node electrode, comprised of said agglomerated metal silicide layer, on said first conductive layer.
A method of fabricating a capacitor structure, for a DRAM cell, on a semiconductor substrate, featuring a storage node electrode, comprised of a agglomerated titanium disilicide layer, on an underlying polysilicon layer, comprising the steps of:
- providing a transfer gate transistor, on said semiconductor substrate, comprised of a polysilicon gate structure on a gate insulator layer, and source and drain regions, in said semiconductor substrate, in regions of said DRAM cell not covered by said polysilicon gate structure;
- depositing a first insulator layer;
- opening a storage node contact hole in said first insulator layer, exposing top surface of said source and drain region;
- depositing a conductive layer on top surface of said first insulator layer, and completely filling said storage node contact hole;
- removing said conductive layer from the top surface of said first insulator layer, forming a conductive plug in said storage node contact hole;
- depositing a first polysilicon layer;
- depositing a second insulator layer;
- patterning of said second insulator layer, and of said first polysilicon layer, to form an insulator mesa overlying, a first polysilicon shape, with said insulator mesa comprised of said second insulator layer, and with said first polysilicon shape, comprised of said first polysilicon layer, contacting underlying, said conductive plug;
- depositing a second polysilicon layer;
- anisotropic etching of said second polysilicon layer, to form polysilicon spacers on the sides of said insulator mesa, and on the sides of said first polysilicon shape;
- removing said insulator mesa from underlying, said first polysilicon shape, resulting in a cylindrical, polysilicon storage node electrode shape, comprised of said polysilicon spacers, extending upwards from said first polysilicon shape;
- depositing a titanium layer;
- a first rapid thermal annealing procedure, performed at a temperature of 750.degree. C., or less, converting said titanium layer, on said cylindrical, polysilicon storage node electrode shape, to a smooth titanium disilicide layer, while leaving said titanium layer, on the top surface of said second insulator layer, unreacted;
- removing said titanium layer from the top surface of said first insulator layer;
- a second rapid thermal annealing procedure, performed at a temperature between about 800 to 1000.degree. C., converting said smooth titanium disilicide layer to said agglomerated titanium silicide layer, resulting in said storage node electrode, comprised of said agglomerated titanium disilicide layer, on said cylindrical, polysilicon storage node electrode shape;
- forming a capacitor dielectric layer on said storage node electrode;
- and
- forming a cell plate electrode, for said capacitor structure.
Dependencies are inferred from the claim text.