Method of producing a through-hole, silicon substrate having a through-hole, device using such a substrate, method of producing an ink-jet print head, and ink-jet print head

A method of producing a through-hole in a silicon substrate, said method comprising the step of:

• (a) forming a dummy layer on the principal surface of said substrate at a location where the through-hole will be formed, said dummy layer being formed on said substrate in an embedded fashion by anodizing said substrate to convert it to a porous material, wherein said dummy layer is capable of being selectively etched without etching the material of said substrate;
• (b) forming a passivation layer having resistance to an etching process on said substrate such that said dummy layer is covered with said passivation layer;
• (c) forming an etching mask layer on the back surface of said substrate, said etching mask layer having an opening corresponding to said dummy layer;
• (d) etching the substrate by means of a crystal orientation-dependent anisotropic etching process until said dummy layer is exposed via said opening;
• (e) removing said dummy layer by etching said dummy layer from the part which has been exposed in said step of etching the substrate;
• and
• (f) partially removing said passivation layer so as to form a through-hole.

A method of producing a through-hole in a silicon substrate, said method comprising the step of:

• (a) forming a dummy layer on the principal surface of said substrate at a location where the through-hole will be formed, said dummy layer comprising silicon dioxide formed by oxidizing porous silicon formed on said substrate in an embedded fashion by anodizing said substrate thereby converting it to porous silicon, wherein the dummy layer is capable of being selectively etched without etching the material of said substrate;
• (b) forming a passivation layer having resistance to an etching process on said substrate such that said dummy layer is covered with said passivation layer;
• (c) forming an etching mask layer on the back surface of said substrate, said etching mask layer having an opening corresponding to said dummy layer;
• (d) etching the substrate by means of a crystal orientation-dependent anisotropic etching process until said dummy layer is exposed via said opening;
• (e) removing said dummy layer by etching said dummy layer from the part which has been exposed in said step of etching the substrate;
• and
• (f) partially removing said passivation layer so as to form a through-hole.

A method of producing a through-hole in a silicon substrate, said method comprising the step of:

• (a) forming a dummy layer on the principal surface of said substrate at a location where the through-hole will be formed, said dummy layer being capable of being selectively etched without etching the material of said substrate;
• (b) forming a passivation layer having resistance to an etching process on said substrate such that said dummy layer is covered with said passivation layer;
• (c) forming an etching mask layer on the back surface of said substrate, said etching mask layer having an opening corresponding to said dummy layer;
• (d) etching the substrate by means of a crystal orientation-dependent anisotropic etching process until said dummy layer is exposed via said opening;
• (e) removing said dummy layer by etching said dummy layer from the part which has been exposed in said step of etching the substrate, wherein a membrane of said passivation layer having a tensile stress is formed;
• and
• (f) partially removing said passivation layer so as to form a through-hole.

A method of producing an ink-jet print head comprising an emission hole for emitting ink, an ink flow path in communication with said emission hole, and a substrate having an emission energy generator for emitting ink and a through-hole serving as an ink supplying hole for supplying ink into said ink flow path, said method comprising the steps of:

• (a) forming a dummy layer on the principal surface of said substrate at a location where the through-hole will be formed, wherein said dummy layer is made of a polycrystalline silicon film, said dummy layer being capable of being selectively etched without etching the material of said substrate;
• (b) forming a passivation layer having resistance to an etching process on said substrate such that said dummy layer is covered with said passivation layer;
• (c) forming an etching mask layer on the back surface of said substrate, said etching mask layer having an opening corresponding to said dummy layer;
• (d) etching the substrate by means of a crystal orientation-dependent anisotropic etching process until said dummy layer is exposed via said opening;
• (e) removing said dummy layer by etching said dummy layer from the part which has been exposed in said step of etching the substrate;
• and
• (f) partially removing said passivation layer so as to form a through-hole serving as said ink supplying hole.

A method of producing an ink-jet print head comprising an emission hole for emitting ink, an ink flow path in communication with said emission hole, and a substrate having an emission energy generator for emitting ink and a through-hole serving as an ink supplying hole for supplying ink into said ink flow path, said method comprising the steps of:

• (a) forming a dummy layer on the principal surface of said substrate at a location where the through-hole will be formed, wherein said dummy layer is formed on said substrate in an embedded fashion by anodizing said substrate thereby converting it to a porous material, said dummy layer being capable of being selectively etched without etching the material of said substrate;
• (b) forming a passivation layer having resistance to an etching process on said substrate such that said dummy layer is covered with said passivation layer;
• (c) forming an etching mask layer on the back surface of said substrate, said etching mask layer having an opening corresponding to said dummy layer;
• (d) etching the substrate by means of a crystal orientation-dependent anisotropic etching process until said dummy layer is exposed via said opening;
• (e) removing said dummy layer by etching said dummy layer from the part which has been exposed in said step of etching the substrate;
• and
• (f) partially removing said passivation layer so as to form a through-hole serving as said ink supplying hole.

A method of producing an ink-jet print head comprising an emission hole for emitting ink, an ink flow path in communication with said emission hole, and a substrate having an emission energy generator for emitting ink and a through-hole serving as an ink supplying hole for supplying ink into said ink flow path, said method comprising the steps of:

• (a) forming a dummy layer on the principal surface of said substrate at a location where the through-hole will be formed, wherein said dummy layer is made up of silicon dioxide formed by oxidizing porous silicon formed on said substrate in an embedded fashion by anodizing said substrate thereby converting it to porous silicon, said dummy layer being capable of being selectively etched without etching the material of said substrate;
• (b) forming a passivation layer having resistance to an etching process on said substrate such that said dummy layer is covered with said passivation layer;
• (c) forming an etching mask layer on the back surface of said substrate, said etching mask layer having an opening corresponding to said dummy layer;
• (d) etching the substrate by means of a crystal orientation-dependent anisotropic etching process until said dummy layer is exposed via said opening;
• (e) removing said dummy layer by etching said dummy layer from the part which has been exposed in said step of etching the substrate;
• and
• (f) partially removing said passivation layer so as to form a through-hole serving as said ink supplying hole.

A method of producing an ink-jet print head comprising an emission hole for emitting ink, an ink flow path in communication with said emission hole, and a substrate having an emission energy generator for emitting ink and a through-hole serving as an ink supplying hole for supplying ink into said ink flow path, said method comprising the steps of:

• (a) forming a dummy layer on the principal surface of said substrate at a location where the through-hole will be formed, said dummy layer being capable of being selectively etched without etching the material of said substrate;
• (b) forming a passivation layer having resistance to an etching process on said substrate such that said dummy layer is covered with said passivation layer;
• (c) forming an etching mask layer on the back surface of said substrate, said etching mask layer having an opening corresponding to said dummy layer;
• (d) etching the substrate by means of a crystal orientation-dependent anisotropic etching process until said dummy layer is exposed via said opening;
• (e) removing said dummy layer by etching said dummy layer from the part which has been exposed in said step of etching the substrate, wherein a membrane of said passivation layer is formed by etching said dummy layer, said membrane of the passivation layer has a tensile stress;
• and
• (f) partially removing said passivation layer so as to form a through-hole serving as said ink supplying hole.

A method of producing an ink-jet print head comprising an emission hole for emitting ink, an ink flow path in communication with said emission hole, and a substrate having an emission energy generator for emitting ink and a through-hole serving as an ink supplying hole for supplying ink into said ink flow path, said method comprising the steps of:

• (a) forming an epitaxial growth preventing layer for preventing epitaxial growth on a part of said substrate, and then forming an epitaxial layer on said substrate thereby forming a dummy layer made of a polycrystalline silicon film, capable of being selectively etched without etching the material of said substrate, said dummy layer being formed on said epitaxial growth preventing layer at a location where the through-hole will be formed;
• (b) forming a passivation layer having resistance to an etching process on said substrate such that said dummy layer is covered with said passivation layer;
• (c) forming an etching mask layer on the back surface of said substrate, said etching mask layer having an opening corresponding to said dummy layer;
• (d) etching the substrate by means of a crystal orientation-dependent anisotropic etching process until said epitaxial growth preventing layer is exposed via said opening;
• (e) removing the part of said epitaxial growth preventing layer exposed in the step of etching the substrate;
• (f) removing said dummy layer by etching it via the removed part of said epitaxial growth preventing layer;
• and
• (g) partially removing said passivation layer so as to form a through-hole.

A method of producing an ink-jet print head comprising an emission hole for emitting ink, an ink flow path in communication with said emission hole, and a substrate having an emission energy generator for emitting ink and a through-hole serving as an ink supplying hole for supplying ink into said ink flow path, said method comprising the steps of:

• (a) forming an epitaxial growth preventing layer for preventing epitaxial growth on a part of said substrate, and then forming an epitaxial layer on said substrate thereby forming a dummy layer made up of silicon dioxide formed by oxidizing porous silicon formed on said substrate in an embedded fashion by anodizing said substrate thereby converting it to porous silicon, wherein said dummy layer is capable of being selectively etched without etching the material of said substrate, said dummy layer being formed on said epitaxial growth preventing layer at a location where the through-hole will be formed;
• (b) forming a passivation layer having resistance to an etching process on said substrate such that said dummy layer is covered with said passivation layer;
• (c) forming an etching mask layer on the back surface of said substrate, said etching mask layer having an opening corresponding to said dummy layer;
• (d) etching the substrate by means of a crystal orientation-dependent anisotropic etching process until said epitaxial growth preventing layer is exposed via said opening;
• (e) removing the part of said epitaxial growth preventing layer exposed in the step of etching the substrate;
• (f) removing said dummy layer by etching it via the removed part of said epitaxial growth preventing layer;
• and
• (g) partially removing said passivation layer so as to form a through-hole.

A method of producing an ink-jet print head comprising an emission hole for emitting ink, an ink flow path in communication with said emission hole, and a substrate having an emission energy generator for emitting ink and a through-hole serving as an ink supplying hole for supplying ink into said ink flow path, said method comprising the steps of:

• (a) forming an epitaxial growth preventing layer for preventing epitaxial growth on a part of said substrate, and then forming an epitaxial layer on said substrate thereby forming a dummy layer capable of being selectively etched without etching the material of said substrate, said dummy layer being formed on said epitaxial growth preventing layer at a location where the through-hole will be formed;
• (b) forming a passivation layer having resistance to an etching process on said substrate such that said dummy layer is covered with said passivation layer,
• (c) forming an etching mask layer on the back surface of said substrate, said etching mask layer having an opening corresponding to said dummy layer;
• (d) etching the substrate by means of a crystal orientation-dependent anisotropic etching process until said epitaxial growth preventing layer is exposed via said opening;
• (e) removing the part of said epitaxial growth preventing layer exposed in the step of etching the substrate;
• (f) removing said dummy layer by etching it via the removed part of said epitaxial growth preventing layer, wherein a membrane of said passivation layer having a tensile stress is formed by etching said dummy layer;
• and
• (g) partially removing said passivation layer so as to form a through-hole.