Process for preparing continuously variable-composition copolymers
AssigneeRohm and Haas Company
InventorsBernard George Kinker, Joseph Martin Bollinger, Robert Howard Gore, David Arthur Pierce
Life of this patent
Estimating the term…
Abstract
A process for the preparation of continuously variable-composition copolymers by effecting gradual changes in monomer composition during the polymerization is disclosed. Poly(meth)acrylate copolymers made by the process of the present invention have improved lubricating oil additive properties, for example, as pour point depressants, when compared to related polymer additives made by conventional means.
Claims16
A process for preparing continuously variable-composition copolymers comprising:
- (a) forming a first reaction mixture comprising a monomer-containing phase in which two or more copolymerizable monomers are present in a weight percent ratio from X.sub.1 /Y.sub.1 to Y.sub.1 /X.sub.1 ;
- (b) forming one or more additional reaction mixtures comprising a monomer-containing phase in which two or more copolymerizable monomers are present in a weight percent ratio from X.sub.n /Y.sub.n to Y.sub.n /X.sub.n ;
- (c) initiating a free-radical addition polymerization by gradual addition of the first reaction mixture or a mixture of the first reaction mixture with the one or more additional reaction mixtures to a reactor under polymerization conditions;
- (d) continuing the polymerization by gradual addition of the one or more additional reaction mixtures
- (i) to the reactor or
- (ii) to the first reaction mixture being added to the reactor at a point prior to where the first reaction mixture is added to the reactor;
- and
- (e) maintaining polymerization conditions until at least 90% of the two or more copolymerizable monomers has been converted to copolymer;
- wherein X.sub.1 and Y.sub.1 represent weight percents of any two X and Y monomers of the two or more copolymerizable monomers in the first reaction mixture;
- wherein X.sub.n and Y.sub.n represent weight percents of any two X and Y monomers of the two or more copolymerizable monomers in the one or more additional reaction mixtures;
- X.sub.1, X.sub.n, Y.sub.1 and Y.sub.n have values from zero to 100 percent;
- n represents successive integers from 2 to 10 corresponding to each of the one or more additional reaction mixtures containing the analogous X.sub.n and Y.sub.n weight percents;
- the maximum value of n represents the total number of reaction mixtures use in the process;
- wherein the gradual addition of the one or more additional reaction mixtures in step (d) is conducted such that at least one of [X.sub.i -X.sub.T ] or [Y.sub.i -Y.sub.T ] absolute values in the reactor is at least 5 percent and X.sub.i, X.sub.T, Y.sub.i and Y.sub.T represent instantaneous weight percents of any two X and Y monomers added to the reactor initially (X.sub.i and Y.sub.i) and at some time later in the polymerization (X.sub.T and Y.sub.T)
- and wherein said copolymer has a weight average molecular weight from 10,000 to 1,000,000;
- and
- said copolymer is soluble in a lubricating oil.
14 more elements
A continuously variable-composition copolymer prepared by:
- (a) forming a first reaction mixture comprising a monomer-containing phase in which two or more copolymerizable monomers are present in a weight percent ratio from X.sub.1 /Y.sub.1 to Y.sub.1 /X.sub.1 ;
- (b) forming one or more additional reaction mixtures comprising a monomer-containing phase in which two or more copolymerizable monomers are present in a weight percent ratio from X.sub.n /Y.sub.n to Y.sub.n /X.sub.n ;
- (c) initiating a free-radical addition polymerization by gradual addition of the first reaction mixture or a mixture of the first reaction mixture with the one or more additional reaction mixtures to a reactor under polymerization conditions;
- (d) continuing the polymerization by gradual addition of the one or more additional reaction mixtures
- (i) to the reactor or
- (ii) to the first reaction mixture being added to the reactor at a point prior to where the first reaction mixture is added to the reactor;
- and
- (e) maintaining polymerization conditions until at least 90% of the two or more copolymerizable monomers has been converted to copolymer;
- wherein X.sub.1 and Y.sub.1 represent weight percents of any two X and Y monomers of the two or more copolymerizable monomers in the first reaction mixture;
- wherein X.sub.n and Y.sub.n represent weight percents of any two X and Y monomers of the two or more copolymerizable monomers in the one or more additional reaction mixtures;
- X.sub.1, X.sub.n, Y.sub.1 and Y.sub.n have values from zero to 100 percent;
- n represents successive integers from 2 to 10 corresponding to each of the one or more additional reaction mixtures containing the analogous X.sub.n and Y.sub.n weight percents;
- the maximum value of n represents the total number of reaction mixtures use in the process;
- wherein the gradual addition of the one or more additional reaction mixtures in step (d) is conducted such that at least one of [X.sub.i -X.sub.T ] or [Y.sub.i -Y.sub.T ] absolute values in the reactor is at least 5 percent and X.sub.i, X.sub.T, Y.sub.i and Y.sub.T represent instantaneous weight percents of any two X and Y monomers added to the reactor initially (X.sub.i and Y.sub.i) and at some time later in the polymerization (X.sub.T and Y.sub.T)
- and wherein said copolymer has a weight average molecular weight from 10,000 to 1,000,000;
- and
- said copolymer is soluble in a lubricating oil.
14 more elements
A method of inhibiting the growth of paraffin crystals in a composition comprising adding to a composition in need thereof, a continuously variable-composition copolymer prepared by:
- (a) forming a first reaction mixture comprising a monomer-containing phase in which two or more copolymerizable monomers are present in a weight percent ratio from X.sub.1 /Y.sub.1 to Y.sub.1 /X.sub.1 ;
- (b) forming one or more additional reaction mixtures comprising a monomer-containing phase in which two or more copolymerizable monomers are present in a weight percent ratio from X.sub.n /Y.sub.n to Y.sub.n /X.sub.n ;
- (c) initiating a free-radical addition polymerization by gradual addition of the first reaction mixture or a mixture of the first reaction mixture with the one or more additional reaction mixtures to a reactor under polymerization conditions;
- (d) continuing the polymerization by gradual addition of the one or more additional reaction mixtures
- (i) to the reactor or
- (ii) to the first reaction mixture being added to the reactor at a point prior to where the first reaction mixture is added to the reactor;
- and
- (e) maintaining polymerization conditions until at least 90% of the two or more copolymerizable monomers has been converted to copolymer;
- wherein X.sub.1 and Y.sub.1 represent weight percents of any two X and Y monomers of the two or more copolymerizable monomers in the first reaction mixture;
- wherein X.sub.n and Y.sub.n represent weight percents of any two X and Y monomers of the two or more copolymerizable monomers in the one or more additional reaction mixtures;
- X.sub.1, X.sub.n, Y.sub.1 and Y.sub.n have values from zero to 100 percent;
- n represents successive integers from 2 to 10 corresponding to each of the one or more additional reaction mixtures containing the analogous X.sub.n and Y.sub.n weight percents;
- the maximum value of n represents the total number of reaction mixtures use in the process;
- wherein the gradual addition of the one or more additional reaction mixtures in step (d) is conducted such that at least one of [X.sub.i -X.sub.T ] or [Y.sub.i -Y.sub.T ] absolute values in the reactor is at least 5 percent and X.sub.i, X.sub.T, Y.sub.i and Y.sub.T represent instantaneous weight percents of any two X and Y monomers added to the reactor initially (X.sub.i and Y.sub.i) and at some time later in the polymerization (X.sub.T and Y.sub.T)
- and wherein said copolymer has a weight average molecular weight from 10,000 to 1,000,000;
- and
- said copolymer is soluble in a lubricating oil.