Friction welding of aluminum alloy hollow members
AssigneeNippon Light Metal Company, Ltd.
InventorsHiroyuki Mochizuki, Harumichi Hino, Masayuki Kobayashi
Life of this patent
Estimating the term…
Abstract
The root shape of a flash formed in the friction-welded joint is controlled by introducing an upset delay time interposed between termination of the friction step and commencement of the upset step and by controlling the upset displacement speed. This provides a friction-welded joint having a tensile strength and a fatigue strength which are comparable with those of TIG- or MIG- welded joints and enables aluminum alloy hollow members to be produced by friction welding instead of TIG or MIG welding. Typically, the upset delay time is 0.4 to 0.8 sec and the upset displacement speed is 5.0 to 70.0 mn/sec to form a flash having a flash root radius of 0.5 mm or more and a flash root angle of 75.degree. or less.
Claims18
A process of friction-welding aluminum alloy hollow members, comprising the steps of:
- making aluminum alloy hollow members abut each other end to end;
- causing friction between the abutting ends by relative rotation between said ends to generate friction heat, thereby heating the abutting ends to a welding temperature;
- and
- upsetting the heated, abutting ends by pressing said ends against each other to extrude a flash therefrom, wherein:
- said flash has a flash root radius of 0.5 mm or more and a flash root angle of 75.degree. or less, said flash root radius and said flash root angle being defined in a plane which contains an axis of said pressing, said flash root radius being a radius of curvature of a surface of the flash in a portion rising from said members and said flash root angle being an acute angle between said surface of the flash and said axis of the pressing.
A process of friction-welding aluminum alloy hollow members, comprising the steps of:
- making said members abut each other end to end;
- causing friction between the abutting ends by relative rotation between said ends to generate friction heat, thereby heating the abutting ends to a welding temperature;
- and
- upsetting the heated, abutting ends by pressing said ends against each other to extrude a flash therefrom, wherein:
- an upset delay time of from 0.4 to 0.8 sec is interposed between completion of said step of causing friction and commencement of said step of upsetting and said step of upsetting includes applying an upset pressure to said members at an upset displacement speed of from 5.0 to 70.0 mm/sec so as to form a flash having a flash root radius of 0.5 mm or more and a flash root angle of 75.degree. or less, said flash root radius and said flash root angle being defined in a plane which contains an axis of said pressing, said flash root radius being a radius of curvature of a surface of the flash in a portion rising from said members and said flash root angle being an acute angle between said surface of the flash and said axis of the pressing.