Glazing layer-forming composition for hot-coating of furnace refractories and method of forming glazing layer
AssigneeAsahi Chemical Co., Ltd.
InventorsSeiichi Sakaguchi, Mitsutoshi Murase
Life of this patent
Estimating the term…
Abstract
Growth of scale on the wall surfaces of high-temperature furnaces is prevented, or the damaged portions are repaired. In addition, the inner wall surfaces of furnaces such as coke furnaces and carbon-firing furnaces, and attachments to furnaces (furnace lids and gas pipes) are protected from deposition of carbon. Glazing layers are formed by application to the refractory surfaces of furnaces of a glazing agent which comprises as a glaze, on an oxide basis, 0-10% by weight of Li.sub.2 O, 0-10% by weight of B.sub.2 O.sub.3, 10-40% by weight of R.sub.2 O (R represents Na or K) and SiO.sub.2 as the balance, wherein the glaze has a melting point of 900.degree. C. or below.
Claims17
A glazing agent for forming a glazing layer which is hot-applied to furnace refractories or which prevents the deposition of carbon on the furnace refractories, the glazing agent consisting essentially of 100 parts or less by weight of a thermal expansively modifier added to 100 parts by weight of a glazing agent which consists essentially of as a glaze of the glazing layer, on an oxide basis, 0-10% by weight of Li.sub.2 O, 0-10% by weight of B.sub.2 O.sub.3, 10-40% by weight of R.sub.2 O wherein R represents Na or K,and SiO.sub.2 as the balance,
- wherein the glaze has a melting point of 900.degree. C. or below.
A glazing agent for forming a glazing layer which is hot-applied to furnace refractories or which prevents the deposition of carbon on the furnace refractories, the glazing agent comprising as a glaze of the glazing layer, on an oxide basis, 0-10% by weight of Li.sub.2 O, 0-10% by weight of B.sub.2 O.sub.3, 10-40% by weight of R.sub.2 O wherein R represents Na or K, and SiO.sub.2 as the balance,
- wherein the glaze has a melting point of 900.degree. C. or below, and
- a compound which forms SiO.sub.2 comprises one or more selected from the group consisting of sodium silicate, potassium silicate and lithium silicate, in addition to an alkali siliconate.
A method of forming a glazing layer which prevents the deposition of carbon on inner wall surfaces of a furnace, the method comprising the steps of:
- hot-applying to the inner wall surfaces, a glazing agent comprising as a glaze of the glazing layer, on an oxide basis, 0-10% by weight of Li.sub.2 O, 0-10% by weight of B.sub.2 O.sub.3, 10-40% by weight of R.sub.2 O wherein R represents Na or K, and SiO.sub.2 as the balance, wherein the glaze has a melting point of 900.degree. C. or below,
- or applying the glazing agent to the inner wall surfaces while at a temperature 500.degree. C. or below, followed by heating;
- and
- forming the glazing layer on the inner wall surfaces by melting.
A glazing agent for forming a glazing layer which is hot-applied to furnace refractories or which prevents the deposition of carbon on the furnace refractories, the glazing agent consisting essentially of as a glaze of the glazing layer, on an oxide basis, 10-40% by weight of R.sub.2 O wherein R represents Na or K, and SiO.sub.2 as the balance,
- wherein the glaze has a melting point of 900.degree. C. or below.
A method of forming a glazing layer which prevents the deposition of carbon on inner wall surfaces of a furnace, the method comprising the steps of:
- hot-applying to the inner wall surfaces, a glazing agent comprising as a glaze of the glazing layer on an oxide basis, 10-40% by weight of R.sub.2 O wherein R represents Na or K, and SiO.sub.2 as the balance, wherein the glaze has a melting point of 900.degree. C. or below, or
- applying the glazing agent to the inner wall surfaces while at a low temperature, followed by heating;
- and
- forming the glazing layer on the inner wall surfaces by melting.
A glazing agent for forming a glazing layer which is hot-applied to furnace refractories or which prevents the deposition of carbon on the furnace refractories, the glazing agent comprises 100 parts or less by weight of a thermal expansively modifier added to 100 parts by weight of a glazing agent which comprises as a glaze of the glazing layer, on an oxide basis, 0.2-10% by weight of Li.sub.2 O, 0-10% by weight of B.sub.2 O.sub.3, 10-40% by weight of R.sub.2 O wherein R represents Na or K, and SiO.sub.2 as the balance,
- wherein the glaze has a melting point of 900.degree. C. or below.
A glazing agent for forming a glazing layer which is hot-applied to furnace refractories or which prevents the deposition of carbon on the furnace refractories, the glazing agent comprises 100 parts or less by weight of a thermal expansively modifier added to 100 parts by weight of a glazing agent which comprises as a glaze of the glazing layer, on an oxide basis, 0-10% by weight of Li.sub.2 O, 0-10% by weight of B.sub.2 O.sub.3, 10-40% by weight of R.sub.2 O wherein R represents Na or K, and SiO.sub.2 as the balance,
- wherein the glaze has a melting point of 900.degree. C. or below, and
- a compound which forms SiO.sub.2 comprises one or more selected from the group consisting of sodium silicate, potassium silicate and lithium silicate, in addition to an alkali siliconate.
A glazing agent for forming a glazing layer which is hot-applied to furnace refractories or which prevents the deposition of carbon on the furnace refractories the glazing agent comprising as a glaze of the glazing layer, on an oxide basis, 10-40% by weight of R.sub.2 O, wherein R represents Na or K and SiO.sub.2 as the balance,
- the glaze has a melting point of 900.degree. C. or below, and
- a compound which forms SiO.sub.2 comprises one or more selected from the group consisting of sodium silicate, potassium silicate and lithium silicate, in addition to an alkali siliconate.
A glazing agent for forming a glazing layer which is hot applied to furnace refractories or which prevents the deposition of carbon on the furnace refractories, the glazing agent comprising as a glaze of the glazing layer, on an oxide basis, 10-40% by weight of R.sub.2 O, wherein R represents Na or K and SiO.sub.2 as the balance,
- the glaze has a melting point of 900.degree. C. or below, and
- a compound which forms R.sub.2 O comprises one or more selected from the group consisting of sodium hydroxide, sodium carbonate, sodium bicarbonate, sodium nitrate, sodium phosphate, sodium sulfate, sodium chloride, sodium silicate, potassium hydroxide, potassium carbonate, potassium bicarbonate, potassium nitrate, potassium phosphate, potassium sulfate, potassium chloride and potassium silicate.
Dependencies are inferred from the claim text.