US 6,054,651 AGranted

Foamed elastomers for wafer probing applications and interposer connectors

AssigneeInternational Business Machines Corporation

InventorsKeith Edward Fogel, James Lupton Hedrick, Paul Alfred Lauro, Yun-Hsin Liao, Da-Yuan Shih

Life of this patent

Estimating the term…

Loading patent…

Abstract

The present invention is directed to a new foamed elastomer composition including elastomer, hollow fillers, and reinforced fillers for supporting the conducting wires in the test probes for wafer level testing and burn in and interposer connector applications. The thermally stable elastomer resin is mixed with hollow fillers and reinforced fillers before filling into the probe or connector mold with an array of elongated conducting wires, then is crosslinked by a crosslinking agent and a catalyst. The use of compressible hollow fillers to foam the elastomer has been successful to enhance the compliance and resilience, and to reduce the thermal expansion, density, and dielectric constant of the elastomer.

Claims7

Dependent claims

An elastomeric foam structure comprising:

an array of elongated electrical connectors embedded in an elastomeric material composition, said elastomeric material composition comprising an elastomer matrix in admixture with hollow filler particles;
said elastomeric material composition is selected from the group consisting of a polysiloxane random copolymer comprising between about 70% to 85% weight percent of dimethylsiloxane and about 15% to 30% diphenylsiloxane natural rubber, styrene-butadiene rubber, polybutadiene rubber, isobutylene-isoprene rubber, ethylene-propylene rubber, nitrile-butadiene rubber, polychloroprene neoprene, chlorosulfonated polyethylene, chlorinated polyethylene, epichlorhydrin elastomer, acrylic elastomers, polysulfide elastomers, silicone elastomers, fluorocarbon elastomers, thermoplastic styrenic polymers, urethane polymers, olefin elastomers, and combinations thereof;
said hollow filler particles each comprising a compressible polymeric shell formed from homo- or copolymers selected from the group consisting of styrene-acrylonitrile, poly(methyl methacrylate), poly(vinylidene chloride), poly(vinyl alcohol), polyaniline, polyimides, polyamides, polycarbonate, polyethylene and silicon rubber;
each said hollow filler particle encapsulating a gas, said hollow filler particle being formed from a solid filler containing a blowing agent, wherein said solid fillers are selected from the group consisting of zinc oxide and ceric dioxide, neodymium oxide, samarium oxide and europium oxide, said blowing agent formed from a material which decomposes upon application of heat or radiation energy;
said elastomeric material composition having been crosslinked by agents selected from the group consisting of methylhydrosiloxane-dimethylsiloxane copolymers, oxygen, peroxides, poly 1,4-polydienes and sulfur;
so that when said elastomeric material composition is subjected to a compressive force, said elastomer material composition returns to its original shape after said compressive force is released, wherein said elastomer material composition has a lower density and coefficient of thermal expansion than said elastomer matrix.

3 more elements

An elastomeric foam structure comprising:

an array of elongated electrical connectors embedded in an elastomeric material composition, said elastomeric material composition comprising an elastomer matrix in admixture with hollow filler particles;
said elastomeric material composition is selected from the group consisting of a polysiloxane random copolymer comprising between about 70% and 85% by weight percent of dimethylsiloxane and about 15% to 30% diphenylsiloxane, natural rubber, styrene-butadiene rubber, polybutadiene rubber, isobutylene-isoprene rubber, ethylene-propylene rubber, nitrile-butadiene rubber, polychloroprene neoprene, chlorosulfonated polyethylene, chlorinated polyethylene, epichlorhydrin elastomer, acrylic elastomers, polysulfide elastomers, silicone elastomers, fluorocarbon elastomers, thermoplastic styrenic polymers, urethane polymers, olefin elastomers, and combinations thereof;
said hollow filler particles each comprising a compressible polymeric shell formed from homo- or copolymers selected from the group consisting of styrene-acrylonitrile, poly(methyl methacrylate), poly(vinyl chloride), poly(vinyl alcohol), polyaniline, polyimides, polyamides, polycarbonate, polyethylene and silicon rubber;
each said hollow filler particle encapsulating a gas, said hollow filler particle being formed from a solid filler containing a blowing agent which decomposes upon application of heat or radiation energy;
each said hollow filler particle encapsulating a gas, said hollow filler particle being formed from a solid filler containing a blowing agent, said blowing agent formed from a material which decomposes upon application of heat or radiation energy;
said elastomeric material composition containing reinforced fillers selected from the group consisting of zinc oxide, ceric dioxide, neodymium oxide, samarium oxide and europium oxide;
said elastomeric material composition having been crosslinked by agents selected from the group consisting of methylhydrosiloxane-dimethylsiloxane copolymers, oxygen, peroxides, poly 1,4-polydienes and sulfur;
so that when said elastomeric material composition is subjected to a compressive force, said elastomeric material composition returns to its original shape after said compressive force is released, wherein said elastomeric material composition has a lower density and coefficient of thermal expansion than said elastomer matrix.

5 more elements