Method for producing complex-shaped objects from laminae
AssigneeApplied Metallurgy Corporation
InventorGunes M. Ecer
Life of this patent
Estimating the term…
Abstract
The process of forming a part from laminae of powders of materials such as metals, ceramics, intermetallics and composites of such materials, that include forming laminae; forming a stack of the laminae characterized as having a configuration from which a part is to be formed; heating the stack to consolidation temperature, and applying pressure to the heated stack to consolidate the laminae in the stack.
Claims39
The process of forming a part from laminae of powders of materials selected from the group consisting of metals, ceramics, intermetallics and composites of such materials, that includes
- a) forming said laminae,
- b) forming a stack of said laminae characterized as having a configuration from which said part is to be formed,
- c) heating said stack to consolidation temperature,
- d) and applying pressure to the heated stack to consolidate the laminae in the stack,
- e) and providing a die cavity, into which the heated laminae are placed, said pressure applied to the laminae stack in the die cavity.
The process of forming a part from laminae of powders of materials selected from the group consisting of metals, ceramics, intermetallics and composites of such materials, that includes
- a) forming said laminae,
- b) forming a stack of said laminae characterized as having a configuration from which said part is to be formed,
- c) heating said stack to consolidation temperature,
- d) and applying pressure to the heated stack to consolidate the laminae in the stack,
- e) and including placing said stack in a metal or ceramic can prior to said heating, and employing a pressure die to pressurize the stack in the can.
The process of forming a part from green powder laminae, the powder selected from the group consisting of metals, ceramics, intermetallics and composites of such materials that includes the steps of
- a) forming said laminae, said laminae having less than theoretical density,
- b) cutting slots in each lamina along surface contours of the part and along separation surfaces, said slots separating the green part from excess material portions,
- c) forming a stack of said laminae in a predetermined order to form said part in green form, and in the process of forming said stack, applying refractory parting compounds on laminae surfaces where bonding is not desired, and filling said slots with refractory parting compounds,
- d) heating said stack to consolidation temperature,
- e) applying pressure to the heated stack to consolidate the laminae in the stack,
- f) separating consolidated excess portions from the consolidated part along surfaces defined by said parting compounds,
- g) and providing a die cavity into which the heated laminae stack is placed, said pressure applied to the laminae stack in the die cavity.
The process of forming a part from green powder laminae said powder selected from the group consisting of metals, ceramics, intermetallics and composites of such materials, that includes the steps of
- a) forming said laminae, said laminae having less than theoretical density,
- b) cutting slots in said laminae along surface contours of the part and along separation surfaces, said slots separating green part from excess material portions,
- c) forming a stack of said laminae in a predetermined order to form said part in green form, and in the process of forming said stack, applying refractory parting compounds on laminae surfaces where bonding is not desired, and filling said slots with refractory parting compounds,
- d) heating said stack to consolidation temperature,
- e) applying pressure to the heated stack to consolidate the laminae in the stack,
- f) separating consolidated excess portions from the consolidated part along surfaces defined by said parting compounds,
- g) and including placing said stack in a metal or ceramic can prior to said heating, and applying pressure in a die cavity to pressurize said stack in said can.
The process of forming a part from green powder laminae said powder selected from the group consisting of metals, ceramics, intermetallics and composites of such materials that includes the steps of:
- a) forming said laminae;
- said laminae having less than theoretical density and substantially the same diameter,
- b) cutting slots in each lamina along surface contours of the part and along separation surfaces;
- said slots separating green part from excess material portions,
- c) forming a stack of said laminae in a predetermined order to form said part in green form, and in the process of forming said stack, applying refractory parting compounds on laminae surfaces where bonding is not desired, and filling said slots with refractory parting compounds,
- d) heating said stack to consolidation temperature,
- e) placing said heated stack in a simple shaped die cavity, said die cavity sized to be slightly larger than the diameter of laminae,
- f) applying pressure to the heated stack to consolidate the laminae in the stack,
- g) and separating excess portions and refractory parting compounds from the consolidated part along surfaces defined by said parting compounds.
The process of forming a part from laminae of powders of materials selected from the group consisting of metals, ceramics, intermetallics and composites of such materials, that includes
- a) forming said laminae,
- b) forming a stack of said laminae characterized as having a configuration from which said part is to be formed,
- c) heating said stack to consolidation temperature,
- d) and applying pressure to the heated stack to consolidate the laminae in the stack,
- e) said process also including first defining a compaction ratio as the ratio of the density of the part after consolidation to green density of the powder laminae before consolidation;
- creating a three-dimensional solid design of the green part which is elongated in the direction of the applied pressure by a factor substantially equal to the compaction ratio;
- dividing the design of the elongated green part into imaginary slices which when assembled together in the correct order would define the elongated green part;
- creating green powder laminae of predetermined density, size and shape in thicknesses corresponding to the thicknesses of the imaginary slices;
- cutting slots into each laminae to delineate surface contours of the green part at successive heights of the elongated green part;
- stacking the laminae in a preselected sequence to form the three-dimensional elongated green part within the inner volume defined by the slots;
- and when stacking said laminae, applying refractory parting compound on surfaces of laminae where bond formation is to be prevented, and filling the slots with a refractory powder;
- heating the laminae stack to a preselected consolidation temperature in a protective atmosphere if necessary;
- placing the heated laminae stack in a die;
- and applying a pressure to the laminae stack in the elongation direction until the green laminae stack is consolidated to a predetermined density;
- separating the consolidated laminae excess portions along the refractory powder filled slots to free the consolidated part located in the center portion of the laminae stack.