Microsphere containing circuit board paper
AssigneeFiberMark, Inc.
InventorUlrich W. Kempf
Life of this patent
Estimating the term…
Abstract
A pre-preg substrate, having a low dielectric constant and containing a substantially uniformly distributed hollow-glass-microsphere filler, and method for making the same. The pre-preg substrate is treated with impregnation and lamination techniques to form a laminate with a low dielectric constant, and good mechanical and electrical properties, suitable as a base material for surface mounted devices in high performance circuits. Improved pre-pregs for making high performance circuit boards and for making surface mounted integrated circuits. Improved high performance circuit boards for making surface mounted integrated circuits.
Claims25
A pre-preg substrate having the form of a non-woven mat, adapted for the manufacture of pre-pregs and laminates for printed circuit boards, said pre-preg substrate comprising a fibrillated fiber matrix, a flocculating agent, and a low dielectric constant filler substantially uniformly distributed throughout said fibrillated fiber matrix.
A pre-preg made by the following method:
- (a) preparing a paper pulp comprising paper fibers;
- (b) refining said paper pulp so as to fibrillate said fibers;
- (c) adding a filler selected from the group consisting of hollow glass microspheres, glass fibers, aramide fibers, polyester fibers, nylon fibers, polytetrafluoroethylene fibers, polyphenolic fibers, acrylic fibers, ceramic fibers and mixtures of any of the foregoing, to form between five and ten percent of said pulp,
- (d) adding an agent selected from the group consisting of silicone resins, epoxy resins, polyamide resins and moisture-resistant melamine resins, to form a stock suspension;
- (e) adjusting the consistency of said stock suspension to be from 3 to 10 grams per liter;
- (f) adding to said stock suspension a flocculating agent to form a flocculated stock;
- (g) passing said flocculated stock over a screen to form a stock layer;
- (h) pressing said stock layer to remove water;
- (i) heat drying said stock layer;
- (j) calendering said stock layer under a pressure suitable to maintain said glass microspheres and said glass fibers intact and to yield a finished sheet of a thickness between ten and forty-five thousandths of an inch;
- (k) wetting said finished sheet with a solution comprising water, methyl alcohol, and phenolic resin so as to yield a wet sheet wherein 6 to 8 percent of said wet sheet is said solution;
- and
- (l) passing said wet sheet through a resin saturation solution comprising resin form the group consisting of phenoxy resin, epoxy resin and polyester resin so as to form a saturated sheet, wherein 60 percent of said saturated sheet is said resin saturation solution;
- (m) drying said saturated sheet at about 180.degree. Celsius so as to dry but not cross link said resin.
A pre-preg comprising:
- a fibrillated fiber matrix;
- a flocculating agent;
- a filler of low dielectric constant stably associated with said fibrillated fiber matrix, and
- a resin selected from the group consisting of phenolic, epoxy, cyanoester, polyimide, polyetherimide, polyphenylene oxide, polyester, polybenzimidazole, polytetrafluoroethylene and polyphenylene sulfide resins.
A laminate board for a printed circuit comprising:
- one or more pre-preg layers;
- each of said pre-preg layers comprising a fibrillated fiber matrix, a filler, a flocculating agent, and a thermosetting resin;
- said filler being a material of low dielectric constant selected from the group consisting of hollow glass microspheres, chopped glass fibers, spun glass fibers, aramide fibers, polyester fibers, nylon fibers, polytetrafluoroethylene fibers, polyphenolic fibers, acrylic fibers, ceramic fibers and mixtures of any of the foregoing and being stably associated with said fibrillated fiber matrix, and
- said resin being selected from the group consisting of phenolic, epoxy, cyanoester, polyimide, polyetherimide, polyphenylene oxide, polyester, polybenzimidazole, polytetrafluoroethylene and polyphenylene sulfide resins.
Dependencies are inferred from the claim text.