US 5,992,268 A · Amorphous diamond coating of blades

Abstract

Improved razors and razor blades and processes for producing razor blades or similar cutting tools with sharp and durable cutting edges, by hard-carbon coating of blades with amorphous diamond, preferably using a filtered cathodic arc plasma source. A coating of amorphous diamond having at least 40 percent sp3 carbon bonding, a hardness of at least 45 gigapascals and a modulus of at least 400 gigapascals is applied to the sharpened edge of a substrate. The substrate may be mechanically honed, and there is no interlayer between the substrate and the amorphous diamond coating. The coating imparts stiffness and rigidity to a thin blade while maintaining a high aspect ratio.

Claims26

Dependent claims

A method for applying a hard carbon coating to a blade having a cutting edge bounded by a first inclined surface and a second inclined surface and an included blade angle enclosed by said first and second inclined surfaces, said method comprising the steps of:

(a) applying an arc discharge to an evaporable carbon surface of a cathode, thereby generating a plasma stream of vaporized carbon in a generally directional stream resolvable into a set of roughly parallel lines,
(b) orienting a blade to be coated within said plasma stream so that an angle measured from a line bisecting said included blade angle and one of said set of roughly parallel lines is within the range of 20.degree. to 90.degree., thereby exposing one of said first and second inclined surfaces of the cutting edge of the blade to the plasma stream at said angle, and
(c) presenting said blade in relation to the plasma stream so that said deposition of vaporized carbon occurs on said first inclined surface of the cutting edge of the blade and on the second inclined surface of the cutting edge of the blade,
wherein said deposition of vaporized carbon on said first and second inclined surfaces of the cutting edge occurs at an approximately equal average rate of deposition.

1 more element

A method for applying a hard carbon coating to a blade having a cutting edge bounded by a first inclined surface and a second inclined surface, said method comprising the steps of:

(a) applying an arc discharge to an evaporable carbon surface of a cathode, thereby generating a plasma stream of vaporized carbon,
(b) orienting a blade to be coated within said plasma stream so that deposition of said vaporized carbon occurs on the cutting edge of the blade, and
(c) presenting said blade in relation to the plasma stream so that said deposition of vaporized carbon occurs on said first inclined surface of the cutting edge of the blade and on the second inclined surface of the cutting edge of the blade,
(d) wherein said deposition of vaporized carbon on said first and second inclined surfaces of the cutting edge occurs at an approximately equal average rate of deposition,
(e) wherein said blade is held within a stack containing a plurality of stacked blades, and said steps of orienting a blade and presenting said blade are performed simultaneously on said plurality of stacked blades,
(f) wherein each of said plurality of blades within said stack has a tip at the juncture of the first and second inclined surfaces of the cutting edge of the blade and the blades are stacked so that the tips describe a plane,
(g) wherein said plasma stream is a generally directional stream resolvable into a set of roughly parallel lines,
(h) wherein said step of orienting a blade further comprises the step of so disposing the blade that an angle defined by a line normal to said plane and one of said set of roughly parallel lines is within the range of 20.degree. to 90.degree., thereby exposing one of said first and second inclined surfaces of the cutting edge of the blade to the plasma stream at said angle,
(i) wherein said step of presenting includes the step of exposing each of the first and second inclined surfaces of the cutting edge of the blade to the plasma stream at said angle,
(j) wherein said step of exposing each of the first and second inclined surfaces of the cutting edge of the blade includes the further step of moving the stack of blades and the plasma stream relative to one another, thereby sequentially exposing each of said first and second inclined surfaces to said plasma stream so that an incremental deposition layer may form on each of said surfaces during said sequential exposure.

7 more elements

A method for applying a hard carbon coating to a blade having a cutting edge bounded by a first inclined surface and a second inclined surface, said method comprising the steps of:

(a) applying an arc discharge to an evaporable carbon surface of a cathode, thereby generating a plasma stream of vaporized carbon,
(b) orienting a blade to be coated within said plasma stream so that deposition of said vaporized carbon occurs on the cutting edge of the blade, and
(c) presenting said blade in relation to the plasma stream so that said deposition of vaporized carbon occurs on said first inclined surface of the cutting edge of the blade and on the second inclined surface of the cutting edge of the blade,
(d) wherein said deposition of vaporized carbon on said first and second inclined surfaces of the cutting edge occurs at an approximately equal average rate of deposition,
(e) wherein said blade is held within a stack containing a plurality of stacked blades, and said steps of orienting a blade and presenting said blade are performed simultaneously on said plurality of stacked blades,
(f) wherein each of said plurality of blades within said stack has a tip at the juncture of the first and second inclined surfaces of the cutting edge of the blade and the blades are stacked so that the tips describe a plane,
(g) wherein said plasma stream is a generally directional stream resolvable into a set of roughly parallel lines,
(h) wherein said step of orienting a blade further comprises the step of so disposing the blade that an angle defined by a line normal to said plane and one of said set of roughly parallel lines is within the range of 20.degree. to 90.degree., thereby exposing one of said first and second inclined surfaces of the cutting edge of the blade to the plasma stream at said angle,
(i) wherein said step of presenting includes the step of exposing each of the first and second inclined surfaces of the cutting edge of the blade to the plasma stream at said angle, and
(j) further including the steps of applying a first voltage bias and then applying a second voltage bias to the blade while said deposition of vaporized carbon is occurring on the blade.

7 more elements

A method for applying a hard carbon coating to a blade having a cutting edge bounded by a first inclined surface and a second inclined surface, said method comprising the steps of:

(a) applying an arc discharge to an evaporable carbon surface of a cathode, thereby generating a plasma stream of vaporized carbon,
(b) orienting a blade to be coated within said plasma stream so that deposition of said vaporized carbon occurs on the cutting edge of the blade, and
(c) presenting said blade in relation to the plasma stream so that said deposition of vaporized carbon occurs on said first inclined surface of the cutting edge of the blade and on the second inclined surface of the cutting edge of the blade,
(d) wherein said deposition of vaporized carbon on said first and second inclined surfaces of the cutting edge occurs at an approximately equal average rate of deposition,
(e) wherein said blade is held within a holder containing a plurality of blades, and said steps of orienting a blade and presenting said blade are performed on said blade while within the holder,
(f) wherein each of said plurality of blades within said holder has a tip at the juncture of the first and second inclined surfaces of the cutting edge of the blade and encloses a first angle defined by the tip and the first and second inclined surfaces,
(g) wherein said plasma stream is a generally directional stream resolvable into a set of roughly parallel lines, and
(h) wherein said step of orienting a blade further comprises the step of so disposing the blade that a second angle defined by a line bisecting said first angle and one of said set of roughly parallel lines is within the range of 20.degree. to 90.degree., thereby exposing one of said first and second inclined surfaces of the cutting edge of the blade to the plasma stream at said angle,
(i) wherein said step of presenting includes the step of exposing each of the first and second inclined surfaces of the cutting edge of the blade to the plasma stream at said angle, and
(j) wherein said step of exposing each of the first and second inclined surfaces of the cutting edge of the blade includes the further step of moving the set of blades and the plasma stream relative to one another, thereby sequentially exposing each of said first and second inclined surfaces to said plasma stream so that an incremental deposition layer may form on each of said surfaces during said sequential exposure.

7 more elements

A method for applying a hard carbon coating to a blade having a cutting edge bounded by a first inclined surface and a second inclined surface, said method comprising the steps of:

(a) applying an arc discharge to an evaporable carbon surface of a cathode, thereby generating a plasma stream of vaporized carbon,
(b) orienting a blade to be coated within said plasma stream so that deposition of said vaporized carbon occurs on the cutting edge of the blade, and
(c) presenting said blade in relation to the plasma stream so that said deposition of vaporized carbon occurs on said first inclined surface of the cutting edge of the blade and on the second inclined surface of the cutting edge of the blade,
(d) wherein said deposition of vaporized carbon on said first and second inclined surfaces of the cutting edge occurs at an approximately equal average rate of deposition,
(e) wherein said blade is held within a holder containing a plurality of blades, and said steps of orienting a blade and presenting said blade are performed on said blade while within the holder,
(f) wherein each of said plurality of blades within said holder has a tip at the juncture of the first and second inclined surfaces of the cutting edge of the blade and encloses a first angle defined by the tip and the first and second inclined surfaces,
(g) wherein said plasma stream is a generally directional stream resolvable into a set of roughly parallel lines, and
(h) wherein said step of orienting a blade further comprises the step of so disposing the blade that a second angle defined by a line bisecting said first angle and one of said set of roughly parallel lines is within the range of 20.degree. to 90.degree., thereby exposing one of said first and second inclined surfaces of the cutting edge of the blade to the plasma stream at said angle,
(i) wherein said step of presenting includes the step of exposing each of the first and second inclined surfaces of the cutting edge of the blade to the plasma stream at said angle,
(j) further including the steps of applying a first voltage bias and then applying a second voltage bias to the blade while said deposition of vaporized carbon is occurring on the blade.

7 more elements

Dependencies are inferred from the claim text.

Amorphous diamond coating of blades

Life of this patent

Amorphous diamond coating of blades

Life of this patent

Abstract

Claims26