US 5,982,056 A · Thermosetting resin composition, electrically insulated coil, electric rotating machine and method for producing same · patentgrep

Loading patent…

Abstract

A highly thermal-conductive and thermal-resistant electrically insulated coil with less outflow of a thermosetting resin composition can be produced, to provide a small-scale, light-weight rotating machine with high power. The thermosetting resin composition comprises (a) a polyfunctional epoxy resin containing three or more p-(2,3-epoxypropoxy) phenyl groups and a group represented by the Chemical formula 1; or an epoxy resin with a naphthalene backbone, represented by the Chemical formula 3, 4 or 5 or an epoxy resin with an anthracene backbone, such as diglycidyl ether of anthracene diol and triglycidyl ether of anthracene triol; (b) a bifunctional epoxy resin containing two p-(2,3-epoxypropoxy) phenyl groups; (c) an acid anhydride curing agent; and (d) a metal acetonate curing catalyst represented by the Chemical formula 2 at 0.1 to 5 parts by weight per 100 parts by weight of the epoxy resins.

Claims16

Dependent claims

A stator of rotating machine, produced by a method comprising the steps of:

incorporating into an iron core slot an electrically insulating coil produced by winding an insulating tape base material around a conductor formed into a defined coil shape, inserting a wedge into an external circumferential groove of the iron core slot to connect the electrical insulating coil to an external end part of the iron core, and thereafter impregnating and curing the electrically insulated coil and the iron core slot in their integrated state with a thermosetting resin composition, wherein as the thermosetting resin composition, use is made of a thermosetting resin composition being at a viscosity of 5 poise or more at 25.degree. C. and a viscosity of 5 poise or less at 60.degree. C. and comprising:
(a) a polyfunctional epoxy resin containing three or more p-(2,3-epoxypropoxy) phenyl groups and a group represented by the Chemical formula 1 as follows:
##STR17## or an epoxy resin with a naphthalene backbone, represented by the Chemical formula 3, 4 or 5 as follows:
##STR18## (wherein "n" and "m" are 1, 2 or 3);
##STR19## (wherein "m" is 0, 1 or 2;
"n", "n'" and "n"" are 1, 2, 3 or 4;
and the groups with "n", "n'" and "n"" may be attached independently to either one ring or both rings of each of the naphthalene rings);
and ##STR20## (wherein R is an alkyl group with 1 to 10 carbon atoms;
"m" is 0, 1 or 2;
"n" is 1, 2 or 3;
"l" and "l'" are 1, 2, 3 or 4;
and the groups with "n", "l" and "l'" may be attached independently to either one ring or both rings of each of the naphthalene rings), or an epoxy resin with an anthracene backbone;
(b) a bifunctional epoxy resin containing two p-(2,3-epoxypropoxy) phenyl groups;
(c) an acid anhydride curing agent;
and
(d) a metal acetonate curing catalyst represented by the Chemical formula 2 as follows:
##STR21## (wherein X and Y represent methyl group or phenyl group:
Me represents Mn. Co, Zn or Zr;
and "n" represents the coordination number at 0.1 to 5 parts by weight per 100 parts by weight of the epoxy resins;
wherein the ratio of the number of the epoxy resins used is 1 to 4, the ratio being represented by the following relationship:
Ratio of number of epoxy resins={(molar number of (b) used).times.(number of epoxy resins in 1 mole of (b))}.div.{(molar number of (a) used).times.(number of epoxy resins in 1 mole of (a))}.

18 more elements

A stator of rotating machine, produced by a method comprising the steps of:

incorporating into an iron core slot an electrical insulating coil produced by winding an insulating tape base material around a conductor formed into a defined coil shape, inserting a wedge into an external circumferential groove of the iron core slot to connect the electrical insulating coil to an external end part of the iron core, and thereafter impregnating and curing the electrical insulating coil and the iron core slot in their integrated state with a thermosetting resin composition, wherein as the insulating tape base material, use is made of an insulating tape base material with a heat conductivity as high as 0.3 to 0.8 W/mK and wherein as the thermosetting resin composition, use is made of a thermosetting resin composition being at a viscosity of 5 poise or more at 25.degree. C. and a viscosity of 5 poise or less at 60.degree. C. and comprising:
(a) a polyfunctional epoxy resin containing three or more p-(2,3-epoxypropoxy) phenyl groups and a group represented by the Chemical formula 1 as follows:
##STR22## or an epoxy resin with a naphthalene backbone triol, represented by the Chemical formula 3, 4 or 5 as follows:
##STR23## (wherein "n" and "m" are 1, 2 or 3);
##STR24## (wherein "m" is 0, 1 or 2;
"n", "n'" and "n"" are 1, 2, 3 or 4;
and the groups with "n", "n'" and "n"" may be attached independently to either one ring or both rings of each of the naphthalene rings);
and ##STR25## (wherein R is an alkyl group with 1 to 10 carbon atoms;
"m" is 0.1 or 2;
"n" is 1, 2 or 3;
"l" and "l'" are 1, 2, 3 or 4;
and the groups with "n", "l" and "l'" may be attached independently to either one ring or both rings of each of the naphthalene rings, or an epoxy resin with an anthracene backbone;
(b) a bifunctional epoxy resin containing two p-(2,3-epoxypropoxy) phenyl groups;
(c) an acid anhydride curing agent;
and
(d) a metal acetonate curing catalyst represented by the Chemical formula 2 as follows:
##STR26## (wherein X and Y represent methyl group or phenyl group;
Me represents Mn, Co, Zn or Zr;
and "n" represents the coordination number) at 0.1 to 5 parts by weight per 100 parts by weight of the epoxy resins;
wherein the ratio of the number of the epoxy resins used is 1 to 4, the ratio being represented by the following relationship:
Ratio of number of epoxy resins={(molar number of (b) used).times.(number of epoxy resins in 1 mole of (b))}.div.{(molar number of (a) used).times.(number of epoxy resins in 1 mole of (a))}.

18 more elements

A stator of rotating machine, produced by a method comprising the steps of:

incorporating, into an iron core slot, an electrical insulating coil produced by winding an insulating tape base material around a stack of insulated conductors formed into a defined coil shape together with a semi-electrically conductive slot liner, inserting a wedge into an external circumferential groove of the iron core slot to connect the electrically insulated coil to an external end part of the iron core, and thereafter impregnating and curing the electrically insulated coil and the iron core slot in their integrated state with a thermosetting resin composition;
wherein as the semi electrical conductive slot liner, use is made of a highly heat-conductive, semiconductive slot liner with a heat conductivity as high as 0.3 to 1.0 W/mK and surface resistance of 0.2 to 100 k.OMEGA.;
and
wherein as the thermosetting resin composition, use is made of a thermosetting resin composition being at a viscosity of 5 poise or more at 25.degree. C. and a viscosity of 5 poise or less at 60.degree. C. and comprising:
(a) a polyfunctional epoxy resin containing three or more p-(2,3-epoxypropoxy) phenyl groups and a group represented by the Chemical formula 1 as follows:
##STR27## or an epoxy resin with a naphthalene backbone, represented by the Chemical formula 3, 4 or 5 as follows:
##STR28## (wherein "n" and "m" are 1, 2 or 3);
##STR29## (wherein "m" is 0, 1 or 2;
"n", "n'" and "n"" are 1, 2, 3 or 4;
and the groups with "n", "n'" and "n"" may be attached independently to either one ring or both rings of each of the naphthalene rings);
and ##STR30## (wherein R is an alkyl group with 1 to 10 carbon atoms;
"m" is 0, 1 or 2;
"n" is 1, 2 or 3;
"l" and "l'" are 1, 2, 3 or 4;
and the groups with "n", "l" and "l'" may be attached independently to either one ring or both rings of each of the naphthalene rings), or an epoxy resin with an anthracene backbone;
(b) a bifunctional epoxy resin containing two p-(2,3-epoxypropoxy) phenyl groups;
(c) an acid anhydride curing agent;
and
(d) a metal acetonate curing catalyst represented by the Chemical formula 2 as follows:
##STR31## (wherein X and Y represent methyl group or phenyl group;
Me represents Mn, Co, Zn or Zr;
and "n" represents the coordination number) at 0.1 to 5 parts by weight per 100 parts by weight of the epoxy resins;
wherein the ratio of the number of the epoxy resins used is 1 to 4, the ratio being represented by the following relationship:
Ratio of number of epoxy resins={(molar number of (b) used).times.(number of epoxy resins in 1 mole of (b))}.div.{(molar number of (a) used).times.(number of epoxy resins in 1 mole of (a))}.

21 more elements

A stator of rotating machine, produced by a method comprising the steps of:

incorporating, into an iron core slot, an electrically insulated coil produced by winding an insulating tape base material around a stack of insulated conductors formed into a defined coil shape together with a semi-electrically conductive slot liner, inserting a wedge into an external circumferentially groove of the iron core slot to connect the electrically insulated coil to an external end part of the iron core, and thereafter impregnating and curing the electrical insulating coil and the iron core slot in their integrated state with a thermosetting resin composition;
wherein as the insulating tape base material, use is made of an insulating tape base material with a heat conductivity as high as 0.3 to 0.8 W/mK;
wherein as the semi electrical conductive slot liner, use is made of a highly heat-conductive, semi-electrically conductive slot liner with a heat conductivity as high as 0.3 to 1.0 W/mK and surface resistance of 0.2 to 100 k.OMEGA.;
and
wherein as the thermosetting resin composition, use is made of a thermosetting resin composition being at a viscosity of 5 poise or more at 25.degree. C. and a viscosity of 5 poise or less at 60.degree. C. and comprising:
(a) a polyfunctional epoxy resin containing three or more p-(2,3-epoxypropoxy) phenyl groups and a group represented by the Chemical formula 1 as follows:
##STR32## or an epoxy resin with a naphthalene backbone, represented by the Chemical formula 3, 4 or 5 as follows:
##STR33## (wherein "n" and "m" are 1, 2 or 3);
##STR34## (wherein "m" is 0, 1 or 2;
"n", "n'" and "n"" are 1, 2, 3 or 4;
and the groups with "n", "n'" and "n"" may be attached independently to either one ring or both rings of each of the naphthalene rings);
and ##STR35## (wherein R is an alkyl group with 1 to 10 carbon atoms;
"m" is 0, 1 or 2;
"n" is 1, 2 or 3;
"l" and "l'" are 1, 2, 3 or 4;
and the groups with "n", "l" and "l'" may be attached independently to either one ring or both rings of each of the naphthalene rings), or an epoxy resin with an anthracene backbone;
(b) a bifunctional epoxy resin containing two p-(2,3-epoxypropoxy) phenyl groups;
(c) an acid anhydride curing agent;
and
(d) a metal acetonate curing catalyst represented by the Chemical formula 2 as follows:
##STR36## (wherein X and Y represent methyl group or phenyl group;
Me represents Mn, Co, Zn or Zr;
and "n" represents the coordination number) at 0.1 to 5 parts by weight per 100 parts by weight of the epoxy resins;
wherein the ratio of the number of the epoxy resins used is 1 to 4, the ratio being represented by the following relationship:
Ratio of number of epoxy resins={(molar number of (b) used).times.(number of epoxy resins in 1 mole of (b))}.div.{(molar number of (a) used).times.(number of epoxy resins in 1 mole of (a))}.

22 more elements

A rotating machine comprising a stator and a rotor, produced by a method comprising the steps of:

incorporating into an iron core slot an electrically insulated coil produced by winding an insulating tape base material around a stack of insulated conductors formed into a defined coil shape, inserting a wedge into an external circumferential groove of the iron core slot to connect the electrical insulating coil to an external end part of the iron core, and thereafter impregnating and curing the electrically insulated coil and the iron core slot in their integrated state with a thermosetting resin composition, wherein as the thermosetting resin composition, use is made of a thermosetting resin composition being at a viscosity of 5 poise or more at 25.degree. C. and a viscosity of 5 poise or less at 60.degree. C. and comprising:
(a) a polyfunctional epoxy resin containing three or more p-(2,3-epoxypropoxy) phenyl groups and a group represented by the Chemical formula 1 as follows:
##STR37## or an epoxy resin with a naphthalene backbone, represented by the Chemical formula 3, 4 or 5 as follows:
##STR38## (wherein "n" and "m" are 1, 2 or 3);
##STR39## (wherein "m" is 0, 1 or 2;
"n", "n'" and "n"" are 1, 2, 3 or 4;
and the groups with "n", "n'" and "n"" may be attached independently to either one ring or both rings of each of the naphthalene rings);
and ##STR40## (wherein R is an alkyl group with 1 to 10 carbon atoms;
"m" is 0, 1 or 2;
"n" is 1, 2 or 3;
"l" and "l'" are 1, 2, 3 or 4;
and the groups with "n", "l" and "l'" may be attached independently to either one ring or both rings of each of the naphthalene rings), or an epoxy resin with an anthracene backbone;
(b) a bifunctional epoxy resin containing two p-(2,3-epoxypropoxy) phenyl groups;
(c) an acid anhydride curing agent;
and
(d) a metal acetonate curing catalyst represented by the Chemical formula 2 as follows:
##STR41## (wherein X and Y represent methyl group of phenyl group;
Me represents Mn, Co, Zn or Zr;
and "n" represents the coordination number) at 0.1 to 5 parts by weight per 100 parts by weight of the epoxy resins;
wherein the ratio of the number of the epoxy resins used is 1 to 4, the ratio being represented by the following relationship:
Ratio of number of epoxy resins={(molar number of (b) used).times.(number of epoxy resins in 1 mole of (b))}.div.{(molar number of (a) used).times.(number of epoxy resins in 1 mole of (a))}.

18 more elements

A stator of rotating machine, produced by a method comprising the steps of:

incorporating into an iron core slot an electrically insulated coil produced by winding an insulating tape base material around a stack of insulated conductors formed into a defined coil shape together with a semi-electrically conductive slot liner, inserting a wedge into an external circumferential groove of the iron core slot to connect the electrically insulated coil to the external end part of the iron core, and thereafter impregnating and curing the electrically insulated coil and the iron core slot in their integrated state with a thermosetting resin composition, wherein as the insulating tape base material, use is made of a corona-resistant polyimide film;
wherein as the semi electrical conductive slot liner, use is made of a highly heat-conductive, semi-electrically conductive slot liner with a heat conductivity as high as 0.3 to 1.0 W/mK and a surface resistance of 0.2 to 100 k.OMEGA.;
and
wherein as the thermosetting resin composition, use is made of a thermosetting resin composition being at a viscosity of 5 poise or more at 25.degree. C. and a viscosity of 5 poise or less at 60.degree. C. and comprising:
(a) a polyfunctional epoxy resin containing three or more p-(2,3-epoxypropoxy) phenyl groups and a group represented by the Chemical formula 1 as follows:
##STR42## or an epoxy resin with a naphthalene backbone, represented by the Chemical formula 3, 4 or 5 as follows:
##STR43## (wherein "n" and "m" are 1, 2 or 3);
##STR44## (wherein "m" is 0, 1 or 2;
"n", "n'" and "n"" are 1, 2, 3 or 4;
and the groups with "n", "n'" and "n"" may be attached independently to either one ring or both rings of each of the naphthalene rings);
and ##STR45## (wherein R is an alkyl group with 1 to 10 carbon atoms;
"m" is 0, 1 or 2;
"n" is 1, 2 or 3;
"l" and "l'" are 1, 2, 3 or 4;
and the groups with "n", "l" and "l'" may be attached independently to either one ring or both rings of each of the naphthalene rings), or an epoxy resin with an anthracene backbone;
(b) a bifunctional epoxy resin containing two p-(2,3-epoxypropoxy) phenyl groups;
(c) an acid anhydride curing agent;
and
(d) a metal acetonate curing catalyst represented by the Chemical formula 2 as follows:
##STR46## (wherein X and Y represent methyl group or phenyl group;
Me represents Mn, Co, Zn or Zr;
and "n" represents the coordination number) at 0.1 to 5 parts by weight per 100 parts by weight of the epoxy resins;
wherein the ratio of the number of the epoxy resins used is 1 to 4, the ratio being represented by the following relationship:
Ratio of number of epoxy resins={(molar number of (b) used).times.(number of epoxy resins in 1 mole of (b))}.div.{(molar number of (a) used).times.(number of epoxy resins in 1 mole of (a))}.

21 more elements

A rotor of rotating machine, produced by a method comprising the steps of:

impregnating and curing an electrically insulated coil produced by winding an insulating tape base material around a stack of insulated conductors formed into a defined coil shape with a thermosetting resin composition, wherein as the insulating tape base material, use is made of a corona-resistant polyimide film, and wherein as the thermosetting resin composition, use is made of a thermosetting resin composition being at a viscosity of 5 poise or more at 25.degree. C. and a viscosity of 5 poise or less at 60.degree. C. and comprising:
(a) a polyfunctional epoxy resin containing three or more p-(2,3-epoxypropoxy) phenyl groups and a group represented by the Chemical formula 1 as follows:
##STR47## or an epoxy resin with a naphthalene backbone triol, represented by the Chemical formula 3, 4 or 5 as follows:
##STR48## (wherein "n" and "m" are 1, 2 or 3);
##STR49## (wherein "m" is 0, 1 or 2;
"n", "n'" and "n"" are 1, 2, 3 or 4;
and the groups with "n", "n'" and "n"" may be attached independently to either one ring or both rings of each of the naphthalene rings);
and ##STR50## (wherein R is an alkyl group with 1 to 10 carbon atoms:
"m" is 0, 1 or 2;
"n" is 1, 2 or 3;
"l" and "l'" are 1, 2, 3 or 4;
and the groups with "n", "l" and "l'" may be attached independently to either one ring or both rings of each of the naphthalene rings);
or an epoxy resin with an anthracene backbone;
(b) a bifunctional epoxy resin containing two p-(2,3-epoxypropoxy) phenyl groups;
(c) an acid anhydride curing agent;
and
(d) a metal acetonate curing catalyst represented by the Chemical formula 2 as follows:
##STR51## (wherein X and Y represent methyl group or phenyl group;
Me represents Mn, Co, Zn or Zr;
and "n" represents the coordination number) at 0.1 to 5 parts by weight per 100 parts by weight of the epoxy resins;
wherein the ratio of the number of the epoxy resins used is 1 to 4, the ratio being represented by the following relationship:
Ratio of number of epoxy resins={(molar number of (b) used).times.(number of epoxy resins in 1 mole of (b))}.div.{(molar number of (a) used).times.(number of epoxy resins in 1 mole of (a))}.

19 more elements

A method for producing a stator of rotating machine, comprising the steps of:

incorporating into an iron core slot an electrically insulated coil produced by winding an insulating tape base material around a stack of insulated conductors formed into a defined coil shape together with a semi-electrically conductive slot liner, inserting a wedge into an external circumferentially groove of the iron core slot to connect the electrical insulating coil to an external end part of the iron core, and thereafter impregnating and curing the electrically insulated coil and the iron core slot in their integrated state with a thermosetting resin composition;
wherein as the insulating tape base material use is made of an insulating tape base material with a heat conductivity as high as 0.3 to 0.8 W/mK;
wherein as the semi-electrically conductive slot liner, use is made of a highly heat-conductive, semi electrical conductive slot liner with a heat conductivity as high as 0.3 to 1.0 W/mK and surface resistance of 0.2 to 100 k.OMEGA.;
and
wherein as the thermosetting resin composition, use is made of a thermosetting resin composition being at a viscosity of 5 poise or more at 25.degree. C. and a viscosity of 5 poise or less at 60.degree. C. and comprising:
(a) a polyfunctional epoxy resin containing three or more p-(2,3-epoxypropoxy) phenyl groups and a group represented by the Chemical formula 1 as follows:
##STR52## or an epoxy resin with a naphthalene backbone, represented by the Chemical formula 3, 4 or 5 as follows:
##STR53## (wherein "n" and "m" are 1, 2 or 3);
##STR54## (wherein "m" is 0, 1 or 2;
"n", "n'" and "n"" are 1, 2, 3 or 4;
and the groups with "n", "n'" and "n"" may be attached independently to either one ring or both rings of each of the naphthalene rings);
and ##STR55## (wherein R is an alkyl group with 1 to 10 carbon atoms;
"m" is 0, 1 or 2;
"n" is 1, 2 or 3;
"l" and "l'" are 1, 2, 3 or 4;
and the groups with "n", "l" and "l'" may be attached independently to either one ring or both rings of each of the naphthalene rings), or an epoxy resin with an anthracene backbone;
(b) a bifunctional epoxy resin containing two p-(2,3-epoxypropoxy) phenyl groups;
(c) an acid anhydride curing agent;
and
(d) a metal acetonate curing catalyst represented by the Chemical formula 2 as follows:
##STR56## (wherein X and Y represent methyl group or phenyl group;
Me represents Mn, Co, Zn or Zr;
and "n" represents the coordination number) at 0.1 to 5 parts by weight per 100 parts by weight of the epoxy resins;
wherein the ratio of the number of the epoxy resins used is 1 to 4, the ratio being represented by the following relationship:
Ratio of number of epoxy resins={(molar number of (b) used).times.(number of epoxy resins in 1 mole of (b))}.div.{(molar number of (a) used).times.(number of epoxy resins in 1 mole of (a))}.

22 more elements

Dependencies are inferred from the claim text.