Double lap joint with welded Z-pins
AssigneeThe Boering Company
InventorJames J. Childress
Life of this patent
Estimating the term…
Abstract
A double shear lap join is formed between metal and composite structure by welding Z-pins in the composite in the joint area to the metal tangs on the metal structure. The joint has modest strength but is less susceptible to shock damage than an adhesive bond or to notch effect crack propagation damage associated with fastened metal/composite joints.
Claims9
A fastener-free structural lap joint for structurally attaching weldable metal structure to fiber-reinforced resin composite structure along an interface, comprising the steps of:
- (a) incorporating metal Z-pin reinforcement in the composite structure in contact with the metal structure in the interface area at an areal density of at least about 2%;
- and
- (b) welding the metal structure to the pins to form a fastener-free lap joint, the pins having a diameter of about 0.20-0.35 inches.
A fastener-free lap joint to connect a fiber-reinforced resin composite to a metal, comprising a product made by:
- at an interface between the composite and the metal, welding Z-pin reinforcement in the composite to the metal, the Z-pin reinforcement being metal fibers having a Young's modulus of at least 10.sup.7 and an areal density of at least about 2%.
A structural joint free of traditional fasteners and joining a fiber-reinforced resin composite and a metal, comprising:
- in an area of overlap between the composite and the metal, a plurality of reinforcing pins of metal fiber at an areal density of at least about 2% embedded in the composite to reinforce the composite, each pin welded to the metal.
Dependencies are inferred from the claim text.