Method of manufacturing fused-magnesia
OwnerHarry B. Shimp, Charles W. Keller +1inventors
InventorsHarry B. Shimp, Charles W. Keller, Steve M. White
Life of this patent
Estimating the term…
Abstract
Undersize particles are recovered from a conventional manufacturing process commonly employed to prepare fused magnesia crystals. The recovery hydrolizes a bulk mass of the collected undersize particles causing fracture to eventually occur in the bulk mass and thereafter fuses the agglomerated material in an electric arc furnace.
Claims2
A process for recovery of pulverized magnesia particles produced by melting in an electric arc furnace having a purity level up to 99 weight percent and a particle size no greater than approximately 250 mesh United States screen size which comprises:
- (a) collecting the magnesia particles in a flexible porous storage container,
- (b) percolating water at ordinary ambient temperature and without mechanical mixing throughout the bulk mass of collected material in an amount from approximately 5 weight percent up to approximately 50 weight percent of the bulk mass of material,
- (c) allowing sufficient time to elapse while the bulk mass of material remains in the storage container at ordinary ambient temperature to cause fracture in the bulk mass of material producing agglomerates ranging in size from approximately one-eighth inch up to approximately two inches,
- (d) removing the agglomerates from the storage container and remelting the agglomerates in an electric arc furnace,
- (e) cooling the remelted magnesia at ordinary ambient temperature to form a solid ingot, and
- (f) pulverizing the solid ingot to form remelted magnesia having a particle size of -40 mesh United states screen size.
Dependencies are inferred from the claim text.