Supplying method for molten alloy for producing amorphous alloy thin strip

A method for supplying molten alloy to a moving cooling substrate for producing an amorphous metal wire or an amorphous metal thin strip comprising:

• providing a ladle for receiving said molten alloy with said ladle having a bottom wall defining a bottom surface of said ladle;
• providing a long nozzle having a length and having an interior passage therein extending the length of said long nozzle, with the length of said interior passage extending in a perpendicular direction or inclined to the perpendicular direction, said long nozzle having one end connected to said bottom wall of said ladle for placing said interior passage of said long nozzle in fluid communication with said molten alloy in said ladle;
• providing a ladle stopper disposed within said ladle, said ladle stopper having an outer wall surface parallel to said perpendicular direction;
• providing a tundish below said ladle and in fluid communication with said long nozzle for receiving molten alloy from a distal end of said interior passage of said long nozzle;
• supplying molten alloy from said ladle to said tundish by feeding molten alloy via said interior passage of said long nozzle;
• supplying molten alloy from said tundish to said moving cooling substrate;
• providing said ladle stopper with a distal end region having a length which is received by said interior passage of said long nozzle at said one end of said long nozzle;
• defining a distance (y) as an overlap distance of the length of said distal end region of said ladle stopper received by said interior passage of said long nozzle during flow of said molten alloy through said interior passage;
• defining an opening area (Ao) which is a sectional area for molten alloy flow provided by the opening area in said interior passage of said long nozzle resulting from receiving said distal end region of said ladle stopper;
• defining a distance (Ln) which is distance from the bottom surface of said ladle to a minimum cross-sectional area of said interior passage of said long nozzle;
• defining a distance (Lm) which is distance from the bottom surface of said ladle to a height of molten alloy in said ladle at start of feed of said molten alloy;
• wherein when (y) is less than 0.1 mm, Ao is set to be less than 1.2 cm.sup.2 and a ratio (Ln)/(Lm) is set to be at least 1.5;
• and
• wherein when (y) is 0.1 to 200 mm, Ao is set to be 0.5 to 10 cm.sup.2.