Reference electrode for monitoring steel-in-concrete potentials

A reference electrode for the measurement of corrosion potentials. said reference electrode consisting essentially of beta-phase manganese dioxide-doped carbon coated with a porous, wetable coating of calcium oxide, silicon dioxide and carbon to provide a combined ceramic electrode structure with a permanent and electrically stable oxygen-catalyst surface equilibrated with air and capable of producing a reversible redox potential, said beta-phase manganese dioxide-doped carbon containing between 1 and 5 weight percent of beta-phase manganese dioxide doped carbon, said beta-phase manganese dioxide-doped carbon produced by treating carbon to improve exchange current density when in equilibrium with air or oxygen, decrease peroxide accumulation and produce manganese dioxide-doped carbon, said treatment consisting of the steps of:

• 1) pretreating said carbon by immersion in a solution of hydrogen peroxide, followed by rinsing and drying to produce pretreated carbon;
• 2) forming an electrochemically stable catalytic surface on said pretreated carbon by impregnating said pretreated carbon with beta-phase manganese by submerging said pretreated carbon in manganese nitrate solution;
• 3) heating said impregnated carbon to between 200 degrees centigrade and 400 degrees centigrade produce carbon doped with with between 1 and 5 weight percent of beta-phase manganese dioxide;
• 4) wetproofing said beta-phase manganese dioxide-doped carbon with a porous fluorocarbon wetproofing film;
• 5) coating said beta-phase manganese dioxide-doped carbon with a porous, wettable coating, said porous wetable coating consisting essentially of calcium oxide, silicon dioxide and carbon,
• whereby said reference electrode for the measurement of corrosion potentials is produced.

A reference electrode for the measurement of corrosion potentials, said reference electrode consisting essentially of beta-phase manganese dioxide-doped carbon as an electrode structure with a permanent and electrically stable oxygen-catalyst surface equilibrated with air and capable of producing a reversible redox potential, said betaphase manganese dioxide-doped carbon containing between 1 and 5 weight percent of beta-phase manganese dioxide doped carbon, said beta-phase manganese dioxide-doped carbon produced by treating carbon to improve exchange current density when in equilibrium with air or oxygen, decrease peroxide accumulation and produce manganese dioxide-doped carbon, said treatment consisting of the steps of:

• 1) pretreating said carbon by immersion in a solution of hydrogen peroxide, followed by rinsing and drying to produce pretreated carbon;
• 2) forming an electrochemically stable catalytic surface on said pretreated carbon by impregnating said pretreated carbon with beta-phase manganese by submerging said pretreated carbon in manganese nitrate solution;
• 3) heating said impregnated carbon to between 200 degrees centigrade and 400 degrees centigrade produce carbon doped with with between 1 and 5 weight percent of beta-phase manganese dioxide;
• 4) wetproofing said beta-phase manganese dioxide-doped carbon with a porous fluorocarbon wetproofing film;
• 5) coating said beta-phase manganese dioxide-doped carbon with a porous, wettable coating, said porous wetable coating consisting essentially of calcium oxide, silicon dioxide and carbon, said calcium oxide of said porous coating being between the limits of 54 and 74 weight percent, said silicon dioxide of said porous coating being between the limits of 13 and 33 weight percent, said carbon of said porous coating is between the limits of 0. 15 and 15 weight percent, and said fluorocarbon wetproofing coating being between 0.0005 and 0.01 inches thick, whereby said reference electrode for the measurement of corrosion potentials is produced.