Method of forming biaxially textured alloy substrates and devices thereon

A biaxially textured allow wherein said allow of texture {100}<100>

• is a Ni allow containing at least one member selected from the group consisting of no more than 15 at % of a Group VB element, no more than 20 at % of Group VIB element, no more than 10 at % of tin (Sn), no more than 10 at % of aluminum (Al), no more than 50 at % of copper (Cu), no more than 25 at % of zinc (Zn), and no more than 12 at % of titanium (Ti), said biaxially textured alloy being characterized by an x-ray diffraction phi scan peak of no more than 30 FWHM, said alloy having a stacking fault frequency parameter less than 0.01 when deformed to at least 60% deformation without any intermediate anneals.

A biaxially textured alloy wherein said alloy of texture {100}<100>

• is formed by rolling and annealing a binary nickel (Ni) alloy containing a member selected from the group consisting of tungsten (W), copper (Cu), aluminum (Al), titanium (Ti), molybdenum (Mo), chromium (Cr), vanadium (V), tantalum (Ta), tin (Sn), and zinc (Zn), said biaxially textured alloy being characterized by an x-ray diffraction phi scan peak of no more than 30 FWHM.

A biaxially textured allow wherein said allow of texture {100}<100>

• is a binary nickel (Ni) allow containing a member selected from the group consiting of tungsten (W), copper (Cu), aluminum (Al), titanium (Ti), molybdenum (Mo), chromium (Cr), vanadium (V), tantalum (Ta), tin (Sn), and zinc (Zn), said biaxially textured alloy being characterized by an x-ray diffraction phi scan peak of no more than 30 FWHM, said alloy having a stacking fault frequency parameter less than 0.01 when deformed to at least 60% deformation by rolling without any intermediate anneals.

A biaxially textured alloy of texture {100}<100>

• formed by rolling and annealing, wherein said alloy is a ternary or quartenary nickel (Ni) alloy containing at least one member selected from the group consisting of tungsten (W), copper (Cu), aluminum (Al), titanium (Ti), molybdenum (Mo), chromium (Cr), vanadium (V), tantalum (Ta), tin (Sn), and zinc (Zn), said biaxially textured alloy being characterized by an x-ray diffraction phi scan peak of no more than 30 FWHM.

A method of forming a biaxially textured alloy article of texture {100}<100>, said biaxially textured alloy being characterized by an x-ray diffraction phi scan peak of no more than 30 FWHM, comprising the steps of:

• providing a sheet of an alloy having a stacking fault frequency parameter of no more than 0.01 after deformation of at least 60% and a recrystallization temperature;
• deforming said alloy to greater than 90% deformation;
• annealing said deformed alloy at a temperature of at least said recrystallization temperature of said alloy.

An biaxially textured alloy formed by rolling and annealing containing at least 60 at % of an FCC metal, said alloy having a stacking fault frequency parameter less than 0.01 when deformed to at least 60% deformation without any intermediate anneals.

A biaxially textured Ni alloy containing a BCC metal, said alloy having a total concentration of any one alloying addition no greater than 20 at %, wherein said texture is formed by rolling and annealing said alloy.

A biaxially textured Ni allow containing a BCC metal, said alloy having a total concentration of any one alloying addition no greater than 20 at %, said alloy having a stacking fault frequency parameter less than 0.01 when deformed to 60% deformation by rolling without any intermediate anneals.