Gas exchange apparatus using improved silicone rubber hollow fiber

A gas exchange apparatus for use as an artificial lung comprising:

• a hollow fiber module formed by bundling a plurality of silicone rubber hollow fibers wound in the form of a twilled pattern, wherein said hollow fiber having not exceeding 400 microns in external diameter, not exceeding 50 microns in rubber thickness, and 100% elongation load strength of not lower than 5 g, composed of a silicone rubber composition including:
• (a) 100 parts by weight of organo-polysiloxane having a viscosity in the range of 10,000 to 10,000,000 poise;
• (b) 5 to 50 parts by weight of organo-polysiloxane copolymer essentially formed of:
• a triorganosiloxy monomer represented by the following formula:
• R.sub.3 SiO.sub.1/2, where R is a non-substituted or substituted monovalent hydrocarbon group having 1 to 10 carbon atoms, and
• a SiO.sub.2 unit;
• and having a molar ratio of said triorganosiloxy monomer relative to said SiO.sub.2 unit being in the range of from 0.6 to 1.2;
• (c) organo-hydrogen siloxane containing at least two hydrogen atoms each being directly coupled with silicon atom, the amount of said siloxane corresponding to that of supplying hydrogen atoms directly coupled with silicon atom being 0.5 to 10 times by mole relative to vinyl groups contained in said components (a) and (b);
• (d) a catalytic quantity of platinum or a platinum compound;
• and
• (e) 100 to 150 parts by weight of finely powdered silica having a specific surface area of not less than 50 m.sup.2 gj;
• a housing for enclosing said hollow fiber module;
• an internal perfusion passage and an external perfusion passage formed within said housing;
• a first inlet and a first outlet formed on said housing for gas or liquid for communication with said internal perfusion passage;
• and
• a second inlet and a second outlet formed on said housing for gas or liquid for communication with said external perfusion passage.