Cellulose acetate with high moldability and process for production thereof

Abstract

Cellulose acetate having a high moldability and low solution viscosity in spite of having a high average degree of polymerization is obtained. The low molecular weight components of cellulose acetate (e.g., CTA having average degree of acetylation of 59.0 to 62.5%) are eluted with a washing solvent to produce a cellulose acetate having a molecular weight distribution Mw/Mn of 1 to 1.7. As the washing solvent, those swell or partially dissolve the cellulose acetate, for example, those which dissolve 0.1 to 30% by weight of cellulose acetate can be used. This solvent includes, for example, a solvent having a solubility parameter .delta. of 7 to 12.5 (ketones, ethers, organic acid, esters, etc.).