Low volatile organic solvent based adhesive
AssigneeThe B.F. Goodrich Company
InventorsCarmen D. Congelio, Andrew M. Olah
Life of this patent
Estimating the term…
Abstract
The present invention relates to a low VOC solvent based adhesive comprising a mixture of at least two organic solvents and a thermoplastic resin. Desirably the adhesive has a flash point of at least 100.degree. F. when measured in accordance with ASTM D3828-87. The solvent blend of the low VOC solvent based adhesive of the instant invention volatilizes at substantially reduced rates as compared to conventional solvent blends in solvent based adhesives. Furthermore, this novel low VOC solvent based adhesive is easy to apply, cost effective, and cures within a reasonable time without the use of heat, ultraviolet light or other mechanical devices. In addition, the novel low VOC solvent based adhesive has good storage stability in metal or non-metal containers.
Claims28
A solvent based adhesive, comprising:
- a) from about 38 to about 75 weight percent of a first solvent being at least one alkyl substituted naphthalene having 1 or more alkyl groups and from 11 to 14 carbon atoms, or at least one alkyl substituted benzene having 1 or more alkyl groups and from 10 to 14 carbon atoms, or combinations thereof, wherein said at least one alkyl substituted naphthalene and/or said at least one alkyl substituted benzene is present in an amount of at least 5 weight percent;
- b) from about 5 to about 20 weight percent of a thermoplastic resin;
- and
- c) from about 5 to about 47 weight percent of an additional one or more solvents
- wherein the weight percent values are based upon the weight of said solvent based adhesive.
A solvent based adhesive, comprising:
- a) from about 38 to about 70 weight percent of at least one alkyl substituted naphthalene having from 11 to 14 carbon atoms and/or alkyl substituted benzene having at least 1 alkyl group and from 10 to 14 carbon atoms,
- b) from about 5 to about 20 weight percent of a chlorinated polyvinyl chloride, and
- c) from about 10 to about 35 weight percent of one or more aliphatic polycarboxylic acids having a total of 4 to 15 carbon atoms, mono or dialkyl esters thereof, having a total of 4 to 19 carbon atoms, alkyl chlorides of said polycarboxylic acids having a total of 4 to 17 carbon atoms, chlorides of said polycarboxylic acids having a total of 4 to 15 carbon atoms or combinations thereof.
A solvent based adhesive, comprising:
- a) from about 38 to about 70 weight percent of at least one alkyl substituted naphthalene having from 11 to 14 carbon atoms and/or alkyl substituted benzene having at least 1 alkyl group and from 10 to 14 carbon atoms,
- b) from about 5 to about 20 weight percent of polyvinyl chloride, and
- c) from about 10 to about 35 weight percent of one or more aliphatic polycarboxylic acids having a total of 4 to 15 carbon atoms, mono or dialkyl esters thereof, said polycarboxylic acids having a total of 4 to 10 carbon atoms, chlorides of said polycarboxylic acids having a total of 4 to 15 carbon atoms or combinations thereof,
- wherein the weight percent values are based upon the weight of said solvent based adhesive.
A solvent based adhesive preparable by a step of mixing a composition comprising:
- a) from about 38 to about 75 weight percent of a first solvent being at least one alkyl substituted naphthalene having 1 or more alkyl groups and from 11 to 14 carbon atoms, or at least one alkyl substituted benzene having 1 or more alkyl groups and from 10 to 14 carbon atoms, or combinations thereof,
- b) from about 5 to about 20 weight percent of a thermoplastic resin;
- and
- c) from about 5 to about 47 weight percent of an additional one or more solvents,
- wherein the weight percent values are based upon the weight of said solvent based adhesive.