Abstract
Carbonated hydroxyapatite compositions and their preparation are described. The compositions are biologically resorbable and are prepared as flowable masses which can be administered by syringe to set in situ to serve as a support structure, filler, prosthesis or the like. Optionally the compositions may include proteins or serve as a depot for compositions of phrarmacological interest.
Claims7
A biologically resorbable paste composition capable of hardening in about 5 to 20 minutes and forming an integral mass, wherein said integral mass:
- (a) is substantially pure carbonate substituted hyhdroxyapatite (Dahllite), having from about 2 to 10% by weight carbonate and a calcium/phosphate ratio in the range of about 1.33-2.0;
- (b) is substantially free of blood and bone marrow;
- (c) is not sintered or hydrothermally prepared;
- (d) has a compressive strength ranging from about 5620 to 11794 psi;
- and
- (e) is biocompatible;
- wherein said paste composition is prepared by the method comprising:
- mechanically mixing under reaction causing conditions at least one calcium source, a partially neutralized phosphoric acid source free of uncombined water, and a carbonate source, with an aqueous lubricant having a pH in the range of about 6-11.
A biologically resorbable paste composition capable of hardening in about 5 to 20 minutes and forming an integral mass, wherein said integral mass:
- (a) is substantially pure carbonate substituted hyhdroxyapatite (Dahllite), having from about 2 to 10% by weight carbonate and a calcium/phosphate ratio in the range of about 1.33-2.0;
- (b) is substantially free of blood and bone marrow;
- (c) is not sintered or hydrothermally prepared;
- (d) has a compressive strength ranging from about 5620 to 11794 psi;
- and
- (e) is biocompatible;
- wherein said paste composition is prepared by the method comprising:
- mechanically mixing under reaction causing conditions at least one calcium source, a partially neutralized phosphoric acid source free of uncombined water, a carbonate source, and an aqueous lubricant having a pH in the range of about 6-11, wherein said lubricant is present in from about 15 to 50 weight % of the total composition.
A biologically resorbable paste composition capable of hardening in about 5 to 20 minutes and forming an integral mass, wherein said integral mass:
- (a) is substantially pure carbonate substituted hyhdroxyapatite (Dahllite), having from about 2 to 10% by weight carbonate and a calcium/phosphate ratio in the range of about 1.33-2.0;
- (b) is substantially free of blood and bone marrow;
- (c) is not sintered or hydrothermally prepared;
- (d) has a compressive strength ranging from about 5620 to 11794 psi;
- and
- (e) is biocompatible;
- wherein said paste composition is prepared by the method comprising:
- combining dry reactants with a liquid lubricant having a pH of in the range from about 6 to 11 to provide a substantially uniform mixture, wherein said dry reactants comprise:
- from about 15 to 35 weight % of a partially neutralized phosphoric acid source;
- from about 50 to 90 weight % of tricalcium phosphate;
- from about 1 to 40 weight % of calcium carbonate;
- and from about 0 to 40 weight % of calcium hydroxide of the dry weight of the dry reactants;
- and said lubricant is present in from about 15 to 50 weight % of said uniform mixture.
Dependencies are inferred from the claim text.