Method for preparing solid solution materials such as lithium manganese oxide
AssigneeNEC Moli Energy (Canada) Limited
InventorsJeffery Raymond Dahn, Erik Rossen, Jan N. Reimers, Eric Wayne Fuller
Life of this patent
Estimating the term…
Abstract
Lithiated manganese oxides are synthesized using a novel two stage process. Using appropriate starting materials, lithiation is accomplished via low temperature ion exchange in aqueous warm salt solution. A drying stage follows which completes the synthesis. Materials suitable for use as cathodes in lithium ion rechargeable batteries have been prepared in this way. Other solid solution transition metal materials might also be prepared using a similar low temperature ion exchange process.
Claims12
A method of preparing a solid solution compound having the formula Li.sub.x MnO2 wherein x is a number in the range from about 0.5 to about 2, which comprises the steps of:
- (a) selecting a manganese oxide hydroxide solid solution starting compound having the formula H.sub.y MnO.sub.2 wherein y is a number in the range from about 1 to about 2;
- (b) selecting an amount of a lithium salt providing in excess of x moles of lithium;
- (c) preparing a mixture of said solid solution starting compound, said amount of lithium salt, and water;
- (d) treating the mixture at a temperature below the decomposition temperature of said solid solution starting compound such that the presence of water is maintained throughout the treating and such that hydrogen ions in said solid starting solution compound are exchanged for lithium to produce an intermediate ion exchanged solid solution compound essentially having the formula H.sub.y-x Li.sub.x MnO.sub.2 and the structure of said solid solution starting compound;
- (e) separating said intermediate ion exchanged solid solution compound from the water and the residual lithium salt in the mixture;
- and
- (f) drying said intermediate ion exchanged solid solution compound so that any remaining hydrogen is removed thereby producing the Li.sub.x MnO.sub.2 solid solution compound.
Dependencies are inferred from the claim text.