Suppression of boron segregation for shallow source and drain junctions in semiconductors

A method for suppressing boron segregation in the manufacturing of a semiconductor having a gate on a gate oxide on a semiconductor substrate, comprising the steps of:

• depositing a screen oxide layer on the semiconductor substrate in contact with the sides of the gate and the gate oxide;
• nitridation of said screen oxide layer with rapid thermal annealing to form a screen oxynitride layer;
• implantation of dopant to form source and drain extension junctions through said screen oxynitride layer at the gate whereby dopant segregation at the gate is prevented;
• depositing a conformal oxide layer on said screen oxynitride layer;
• etching said screen oxynitride layer and said conformal oxide layer until the top of the gate and portions of said source and drain extension junctions are exposed while the sides of the gate remain covered by said conformal oxide layer;
• depositing a second screen oxide layer over said conformal oxide layer, the gate, the gate oxide, and said source and drain extension junctions;
• nitridation of said second screen oxide layer with rapid thermal annealing to form a second screen oxynitride layer;
• and
• implantation of dopant through said second screen oxynitride layer into the semiconductor substrate to form source and drain junctions spaced away from the gate.

A method for suppressing boron segregation in the manufacturing of a semiconductor processed to the placement of a transistor gate over an oxide layered N.sup.- silicon substrate, comprising the steps of:

• chemical vapor deposition of a screen oxide layer over the transistor gate and the oxide layered N.sup.- silicon substrate:
• nitridation of said screen oxide layer by rapid thermal annealing at around 900.degree. C. for 30 seconds in a gaseous nitrogen compound ambient to form a screen oxynitride layer;
• implantation of boron dopant to form P-silicon source and drain extension junctions through said screen oxynitride layer in N.sup.- silicon substrate next to the gate;
• depositing a conformal oxide layer over said screen oxynitride layer;
• etching said conformal oxide layer and said screen oxynitride layer to form a spacer against the sidewalls of the gate and to expose the top of the gate and said source and drain extension junctions away from the gate;
• depositing a second screen oxide layer over said conformal oxide layer, the gate and said source and drain extension junctions;
• second nitridation of said second screen oxide layer by rapid thermal annealing at around 900.degree. C. for 30 seconds in a gaseous nitrogen compound ambient to form a second screen oxynitride layer;
• second implantation of boron dopant through said second screen oxynitride layer to deepen portions of said P-silicon source and said drain junctions in the N.sup.- silicon substrate away from the gate;
• rapid thermal annealing at around 1050.degree. C. for 30 seconds in a gaseous nitrogen ambient to activate said boron;
• and
• removal of said second screen oxynitride layer.