US 5,958,362 A · Method of producing active material powder for lithium secondary battery

Abstract

The present method is to produce an active material powder formed of a spinel oxide containing lithium or a layer-structured oxide containing lithium for a lithium secondary battery which is uniform in composition, fine in particle size and free of oxygen defects, and which is unlikely to cause capacity deterioration resulted from repetitive charge/discharge cycles at a high current density. A suspension 1 prepared by suspending an ingredient of the active material powder in a combustible liquid or an emulsion prepared by emulsifying a solution of the ingredient in the combustible liquid is sprayed in a droplet state 15 together with an oxygenic gas 2. The combustible liquid contained in the droplet 15 is burned to have the ingredient therein reacted and to evaporate the solvent. As a result, active material powder 4 formed of the spinel oxide containing lithium is obtained. An active material powder formed of the layer-structured oxide containing lithium is obtained by re-heating the oxide powder that has been generated by spraying and burning the droplet.

Claims13

Dependent claims

A method of producing a powder of a spinel oxide containing lithium and at least one other metal, for a lithium secondary battery, comprising the steps of:

preparing an aqueous solution comprising lithium ions and ions of at least one other metal where the lithium ions are provided by a compound selected from the group consisting of Li oxide, Li hydroxide, Li carbonate, Li nitrate, Li sulfate, Li acetate and Li oxalate and where the other metal ions are selected from at least one element of the group consisting of Mn, Ni, Co, Ti, V, Al, Zn, Mo, Cu, Fe and Cr and are provided by a compound selected from the group consisting of oxide, hydroxide, carbonate, nitrate, sulfate, acetate and oxalate of said metal or mixtures thereof;
forming an emulsion from said solution with a combustible organic liquid;
spraying said emulsion in the form of droplets into a reaction chamber containing an amount of oxygen sufficient to provide a partial pressure of oxygen of 20% or more as measured in the exhaust gas from said chamber to produce a lithium spinel free of oxygen defects;
burning said combustible liquid contained in said droplets at a temperature of 300.degree. C. to 1200.degree. C. and reacting said ingredients contained therein to produce a powder formed of a spinel oxide containing lithium.

1 more element

Dependencies are inferred from the claim text.

Method of producing active material powder for lithium secondary battery