Ceramic matrix composite and method of manufacturing the same

A ceramic matrix composite comprising:

• a ceramic matrix comprising SiC as a main component, the SiC being formed by reaction sintering of molten Si and C powder;
• ceramic fibers within said ceramic matrix wherein said ceramic fibers are selected from the group consisting of silicon-carbide fibers, silicon-nitride fibers, alumina fibers, and zirconia fibers, and wherein the percentage of said fibers ranges from 10% by volume to 50% by volume of said composite;
• a sliding coating layer covering the ceramic fibers, for facilitating sliding between said ceramic matrix and said ceramic fibers, and wherein said sliding coating layer comprises boron nitride;
• and
• a barrier layer for coating an outer surface of said sliding coating layer to suppress a reaction between said sliding coating layer and Si infiltration of the fibers, wherein said barrier layer comprises a second coating on the fiber surface and is selected from the group consisting of Si, C, Mo, and MoSi.sub.2 ;
• a reaction-preventing component in said ceramic matrix for preventing said sliding coating layer from reacting with the molten Si during reaction sintering, wherein said reaction-preventing component comprises a compound or element from said sliding coating layer and said reaction-preventing component exists within the ceramic matrix in a compound with Si, said Si compound resulting from the reaction sintering, and further wherein the reaction-preventing component comprises B, and said Si compound comprises a Si--B alloy surrounding barrier coating layer,
• and further wherein at least the Si--B alloy surrounding barrier coating layer surrounding said barrier layer has a B concentration less than or equal to the solid saturation value of the B in the molten Si.

A method of manufacturing a ceramic matrix composite comprising the steps of:

• forming a sliding coating layer on surfaces of ceramic fibers by a method selected from the group consisting of CVD, sputtering, and sol-gel, wherein said sliding coating layer consists of boron nitride, and wherein said ceramic fibers are selected from the group consisting of silicon-carbide fibers, silicon-nitride fibers, alumina fibers, and zirconia fibers;
• forming a yarn by gathering said coated fibers;
• forming a preform by casting said yarn in a mold;
• adding C powder to said preform;
• heating Si and a material comprising at least one selected from the group consisting of BN, B.sub.4 C, and B.sub.2 O.sub.3 to fuse said Si and said material;
• and
• infiltrating the resulting molten Si and molten material into said preform, thereby reaction sintering said molten Si and said C powder and reacting said molten Si and said material with each other before said molten Si and said sliding coating layer react with each other, thus preventing said sliding coating layer from eluting in the molten Si.

A method of manufacturing a ceramic matrix composite comprising the steps of:

• forming a sliding coating layer on surfaces of ceramic fibers by a method selected from the group consisting of CVD, sputtering, and sol-gel, wherein said sliding coating layer consists of boron nitride, and further wherein said ceramic fibers are selected from the group consisting of silicon-carbide fibers, silicon-nitride fibers, alumina fibers, and zirconia fibers;
• forming a barrier layer covering said sliding coating layer by a method selected from the group consisting of CVD, sputtering, and sol-gel, wherein said barrier layer is selected from the group consisting of SiC, C, Mo, and MoSi.sub.2 ;
• forming a yarn by gathering said coated fibers;
• forming a preform by casting said yarn in a mold;
• adding C powder to said preform;
• heating Si and a material comprising at least one selected from the group consisting of BN, B.sub.4 C, and B.sub.2 O.sub.3 to fuse said Si and said material;
• and
• infiltrating the resulting molten Si and molten material into said preform, thereby reaction sintering said molten Si and said C powder, and reacting said molten Si and said material with each other before said molten Si and said barrier layer react with each other, thus preventing said barrier layer from eluting in the molten Si.