Abstract
A method of protecting reinforced concrete structures comprising of applying a protective cathodic coating containing a non-corroding metal and an electrochemically active material on concrete wherein the protective coating is formed by thermally spraying a mixture of said non-corroding metal such as a valve metal and said electrochemically active material. The coating may also be formed by applying a precursor of the electrochemically active material and a metal-containing layer to concrete, then anodically polarizing said metal layer to convert the precursor into an electrochemically active material.
Claims12
The method of protecting reinforced concrete with cathodic protection coating on a surface of said concrete, which method comprises thermally spraying together an electrochemically active material and a non-corroding metal onto a surface of said concrete.
In the method of cathodically protecting reinforced concrete with a non-corroding, electrochemically active coating which is present as a metal-containing coating on the surface of said concrete, which metal-containing coating initially contains a metal-containing layer having at its surface a material comprising a precursor composition convertible to an electrochemically active ingredient for said metal-containing coating, the improvement in said method comprising establishing on said concrete such metal-containing layer along with said precursor composition, connecting said metal of the metal-containing layer in an electrical circuit, and anodically polarizing said metal to convert said precursor composition to an electrochemically active ingredient.
The method of protecting reinforced concrete with a cathodic protection coating by applying an adherent, non-corroding and electrochemically active metallic coating to a surface of a concrete substrate, which method comprises:
- roughening the surface of said concrete by abrading said surface and freshly exposing a concrete surface;
- and
- thermally spraying a valve metal selected from the group consisting of titanium, tantalum, niobium, zirconium, hafnium, molybdenum, tungsten, alloys of same and intermetallic mixtures, onto the resulting roughened surface with a spray gun in an amount of sprayed metal having a thickness of from about 20 microns to about 200 microns;
- wherein said spraying comprises:
- applying said metal onto said concrete at a standoff from the surface of said concrete within the range of from about 21/2 inches to about 6 inches;
- while
- conducting said spraying at an application rate across the concrete surface at a speed within the range of from about 100 to about 800 millimeters per second.