Method for making white zeolitic detergent builder from using a solid particulate source of alumina
OwnerAhmad Moini, Christopher R. Castellano +1inventors
InventorsAhmad Moini, Christopher R. Castellano, Steven M. Kuznicki
Life of this patent
Estimating the term…
Abstract
This invention relates to zeolitic molecular sieve compositions characterized by outstanding capability to complex multivalent cations, especially calcium. In particular, the invention relates to novel zeolitic molecular sieve compositions, having a high alumina-to-silica ratio, with additional occluded non-zeolitic silicate, and solid particulate alumina is the source of alumina in the zeolite.
Claims9
A method for producing a synthetic zeolitic molecular sieve having the molar formula:
- 1.25.+-.0.25Na.sub.2 O:1.00Al.sub.2 O.sub.3 :2.10-2.90SiO.sub.2 :1-4H.sub.2 O
- wherein from 5 to 40% of the SiO.sub.2 by weight is nonzeolitic silicate, said method comprising:
- (a) forming a reaction mixture by mixing sodium hydroxide and sodium silicate in the presence of water and heating for at least 5 minutes, said mixture having a molar ratio of Na.sub.2 O/SiO.sub.2 in the range of 0.6 to 2.5, adding to said heated mixture
- (b) additional sodium silicate such that the resulting mixture has a Na.sub.2 /SiO.sub.2 molar ratio of 0.7 to 1.5 and
- (c) at least one source of solid hydrated amorphous alumina or solid hydrated crystalline alumina in amount such that the SiO.sub.2 /Al.sub.2 O.sub.3 ratio of the mixture is in the range of 2.0 to 4.5, and maintaining the mixture at elevated temperature until crystals of silica enriched zeolitic molecular sieve are formed.
Particles of a crystalline zeolitic molecular sieve composition having the x-ray pattern of type B zeolite and containing from 5 to 40% by weight of the silicate present as non-zeolitic silica in addition to the SiO.sub.2 in the framework of type B zeolite crystals, said particles having a GE brightness of at least 90%.
Dependencies are inferred from the claim text.