Pressure sensitive adhesive compositions
AssigneeNational Starch and Chemical Investment Holding Corporation
InventorsLien Phan, Rajeev Farwaha, Patrick J. Hayes
Life of this patent
Estimating the term…
Abstract
The invention relates to a pressure sensitive adhesive prepared from an aqueous emulsion polymer. The polymer is prepared by reacting at least one ethylenically unsaturated monomer and from about 0.1 to about 5 weight percent, based on the total weight of ethylenically unsaturated monomer, of a water-soluble or water-dispersible polymerizable surfactant having a terminal allyl amine moiety. The pressure sensitive adhesives may be used in all types of tapes, labels, decals, packaging, electrical insulation, and surgical bandaging.
Claims28
A pressure sensitive adhesive composition comprising an aqueous emulsion polymer, said polymer comprising the reaction product of at least one ethylenically unsaturated monomer and from about 0.1 to about 5 weight percent, based on the total weight of ethylenically unsaturated monomer, of a water-soluble or water-dispersible polymerizable surfactant having a terminal allyl amine moiety, wherein the polymerization is conducted at a pH of about 2 to about 7.
A method of making a pressure sensitive adhesive, said method comprising
- (I) mixing an acidic metal salt curing agent with an aqueous emulsion polymer to form an adhesive, said polymer comprising the reaction product of at least one ethylenically unsaturated monomer and from about 0.1 to about 5 weight percent, based on the total weight of ethylenically unsaturated monomer, of a water-soluble or water-dispersible polymerizable surfactant having a terminal allyl amine moiety, wherein the polymerization is conducted at a pH of about 2 to about 7;
- (II) applying the adhesive formed in Step (I) to a substrate;
- and
- (III) allowing the adhesive to air cure or using radio frequency to cure the adhesive.
A tape comprising a backing coated with a pressure sensitive adhesive wherein the pressure sensitive adhesive comprises an aqueous emulsion polymer, said polymer comprising the reaction product of at least one ethylenically unsaturated monomer and from about 0.1 to about 5 weight percent, based on the total weight of ethylenically unsaturated monomer, of a water-soluble or water-dispersible polymerizable surfactant having a terminal allyl amine moiety, wherein the polymerization is conducted at a pH of about 2 to about 7.
A substrate comprising a pressure sensitive adhesive wherein the pressure sensitive adhesive comprises an aqueous emulsion polymer, said polymer comprising the reaction product of at least one ethylenically unsaturated monomer and from about 0.1 to about 5 weight percent, based on the total weight of ethylenically unsaturated monomer, of a water-soluble or water-dispersible polymerizable surfactant having a terminal allyl amine moiety, wherein the polymerization is conducted at a pH of about 2 to about 7.
Dependencies are inferred from the claim text.