Method for forming a composite structure

A method for providing a composite structure comprising the steps of:

• providing a core structure formed from a non-metallic composite material in an uncured state;
• applying a fluoroelastomer film in an uncured state over surface portions of said core structure;
• placing a metallic structure over a portion of said core structure, said metallic structure having inner surfaces which contact said fluoroelastomer film;
• molding said composite structure under conditions of heat and pressure for a time sufficient to co-cure said fluoroelastomer film and said non-metallic core structure material and to form a bond between said fluoroelastomer film and said inner surface of said metallic structure;
• activating the inner surfaces of said metallic structure prior to said placing step;
• and
• said activating step comprising cleaning said inner surfaces and etching said inner surfaces so as to remove unwanted oxides and other deleterious materials and further comprising priming said inner surfaces by applying an epoxy resin solution containing an insoluble corrosion inhibitor to said inner surfaces so as to substantially prevent the formation of unwanted oxides on and to improve the bonding characteristics of said inner surfaces.

A method for manufacturing a fan exit guide vane comprising:

• providing a core structure formed from a graphite epoxy material;
• applying a film of a fluoroelastomer based on a copolymer of vinylidene fluoride and hexafluoropropylene or a terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene to surface portions of said core structure;
• placing a metallic leading edge structure over leading edge portions of said core structure covered with said fluoroelastomer film;
• placing the assembly of said core structure, said fluoroelastomer film, and said metallic structure in a mold and co-curing said core structure and said fluoroelastomer film material and bonding said metallic leading edge structure to said core structure by applying heat and pressure to the assembly for a time sufficient to effect said co-curing and said bonding.

A method for manufacturing a fan guide exit vane comprising:

• providing a core structure formed from a graphite epoxy material;
• applying a film of a fluoroelastomer based on a copolymer of vinylidene fluoride and hexafluoropropylene or a terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene to surface portions of said core structure;
• placing a metallic leading edge structure over leading edge portions of said core structure covered with said fluoroelastomer film;
• co-curing said core structure and said fluoroelastomer film material and bonding said metallic leading edge structure to said core structure by placing said core structure with said fluoroelastomer film and said overlaid metallic leading edge structure in a mold and applying heat and pressure for a time sufficient to effect said co-curing and said bonding;
• said leading edge structure placing step comprising placing a stainless steel leading edge structure over said leading edge portion of said core structure;
• pretreating said stainless steel leading edge structure prior to placing it over said leading edge portion of said core structure;
• and
• said pretreating step comprising wiping inner surfaces of said stainless steel leading edge structure with an isopropyl alcohol solution, etching said stainless steel leading edge structure in a ferric chloride etching solution at room temperature for a time period in the range of about 14 to about 16 minutes, and thereafter priming said inner surfaces with an epoxy resin solution containing an insoluble corrosion inhibitor.

A method for fabricating a fan exit guide vane comprising:

• providing a core structure formed from a graphite epoxy material;
• applying an adhesive film of a fluoroelastomer based on a copolymer of vinylidene fluoride and hexafluoropropylene or a terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene to surface portions of said core structure;
• placing a stainless steel leading edge structure over leading edge portions of said core structure covered with said adhesive film;
• and
• placing the assembly of said core structure, said adhesive film, and said stainless steel leading edge structure in a mold and co-curing said core structure and said adhesive film and bonding said stainless steel leading edge structure to said core structure by applying heat and pressure to the assembly for a time sufficient to effect said co-curing and said bonding.

A method for fabricating a fan exit guide vane comprising:

• providing a core structure formed from a graphite epoxy material;
• applying an adhesive film of a fluoroelastomer based on a copolymer of vinylidene fluoride and hexafluoropropylene or a terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene to surface portions of said core structure;
• placing a stainless steel leading edge structure over leading edge portions of said core structure covered with said adhesive film;
• co-curing said core structure and said adhesive film and bonding said stainless steel leading edge structure to said core structure by placing said core structure with said adhesive film and said overlaid stainless steel leading edge structure in a mold and applying heat and pressure for a time sufficient to effect said co-curing and said bonding;
• pretreating said stainless steel leading edge structure prior to placing it over said leading edge portion of said core structure;
• and
• said pretreating step comprising wiping inner surfaces of said stainless steel leading edge structure with an isopropyl alcohol solution, etching said stainless steel leading edge structure in a ferric chloride etching solution at room temperature for a time period in the range of about 14 to about 26 minutes, and thereafter priming said inner surfaces with an epoxy resin solution containing an insoluble corrosion inhibitor.