Plasma sprayed mullite coatings on silicon based ceramic materials

A method for plasma spraying a mullite coating onto a surface of a silicon based ceramic substrate, comprising the steps of:

• maintaining a plasma spray gun nozzle outlet within a distance of from about 1 to 10 inches from the surface to be sprayed, wherein a flame exits from said outlet and at least temporarily resides against the surface to be sprayed;
• maintaining the thermal energy of the plasma flame in a range from about 25 to 45 kW power;
• moving said surface to be sprayed and said outlet relative to one another to limit the residence time of the flame against said surface;
• heating said surface to be sprayed to a temperature sufficient to minimize stresses due to coefficient of thermal expansion and temperature changes of the coating and substrate during deposition wherein said temperature is below the crystallization temperature of mullite;
• introducing a fused and crushed mullite powder of a particle size between about 10 and 250 microns into the flame at a powder feed rate of between about one and several hundred grams per minute;
• whereby the mullite powder particles are not heated to such a high temperature as to cause excessive dissociation of the mullite within the flame but sufficiently high to melt said surfaces of said particles;
• and
• whereby the applied coating is at least 85% by volume crystalline mullite and about 0.5% to about 15% by volume amorphous material and dissociated phases of mullite.

A method for plasma spraying a mullite coating onto a surface of a silicon based ceramic substrate, comprising the steps of:

• maintaining a plasma spray gun nozzle outlet within a distance of less than 4 inches from the surface to be sprayed, wherein a flame exits from said outlet;
• mounting said substrate onto a rotating fixture and moving said surface to be sprayed in a circular path relative to said nozzle outlet at a speed of from about 20 to 100 revolutions per minute;
• heating said surface to be sprayed to a temperature of between about 1550.degree. F. and 1720.degree. F.;
• introducing a fused and crushed mullite powder of a particle size within the range of from about 16 microns to about 176 microns with an average of about 62 microns into the flame at a powder feed rate of from about 20 grams per minute to about 100 grams per minute;
• whereby the mullite powder particles are not heated to such a high temperature as to cause excessive dissociation of the mullite within the flame but sufficiently high to melt said surfaces of said particles;
• and
• the applied coating is at least 85% crystalline mullite and about 0.5% to about 15% by volume amorphous material and dissociated phases of mullite.