US 5,869,141 A · Surface pretreatment for sol coating of metals

Abstract

A surface treatment, especially for titanium and aluminum alloys, forms a sol-gel film covalently bonded on the metal surface to produce strong, durable adhesive bonds between the metal and an organic adhesive without using toxic chemicals and while significantly reducing or eliminating rinse water requirements of traditional anodizing or etching processes. An aqueous sol containing an zirconium and an organosilane with an organic acid catalyst and alkoxyzirconium stabilizer is applied to etched or grit blasted substrates by dipping, spraying, or drenching, to produce bonds in a single application comparable in strength and performance to standard anodize controls. Parameters affecting performance include the sol composition, the Si/Zr ratio, the ratio of sol ingredients, the concentration of the sol, the carrier solvent, solution age, catalysts, surface pretreatment, application method, curing process, and primer used.

Claims9

Dependent claims

A method for promoting adhesion between a metal and an organic resin in a metal-resin hybrid laminate, comprising the steps of:

(a) pretreating the metal to obtain a clean, active surface by:
degreasing the metal;
immersing the degreased metal in alkaline cleaner;
etching the cleaned metal in alkaline;
and
desmutting the etched metal;
(b) coating at least a portion of the active surface of the metal with a water-based sol initially alcohol-free containing about 1 vol % n-alkoxyzirconium sufficient to minimize diffusion of oxygen to the metal surface, about 2 vol % of a reactive organosilane, and an effective amount of glacial acetic acid sufficient to serve both as a catalyst and as a zirconium hydrolysis stabilizer to produce a sol-gel film on at least a bonding surface of the metal;
(c) applying the organic resin, including a functional group for covalently bonding to the organosilane, to the coated bonding surface;
and
(d) covalently bonding the organosilane with the resin.

7 more elements

Dependencies are inferred from the claim text.

Surface pretreatment for sol coating of metals