Abstract
Pb-Ca battery grids are dipped into a bath of molten Pb-Sn or Pb-Ag to prolong the useful life of the battery as determined by the high temperature SAE J240 test.
Claims3
A method of extending the high temperature cycle life of a lead-acid storage battery having a positive electrode comprising a leady active material embedding a current collecting grid comprising a lead-calcium alloy, comprising the steps of:
- forming a strip of said lead-calcium alloy;
- immersing said strip into a melt of a molten coating alloy selected from the group consisting of lead-antimony lead-silver alloys for a time sufficient for said coating alloy to coat and rise to the surface of said strip without completely melting said lead-calcium alloy;
- removing the coated strip from said melt;
- and
- cooling the coated strip to solidify said coating on said surface.
A method of extending the high temperature cycle life of a lead-acid storage battery having a positive electrode comprising a leady active material embedding a current collecting grid comprising a lead-calcium alloy, comprising the steps of:
- forming a ribbon of grid substrate material comprising said lead-calcium alloy,
- immersing said lead-calcium ribbon into a melt of a molten coating alloy selected from the group consisting of lead-antimony and lead-silver alloys for a time sufficient for said coating alloy to coat and fuse to the surface of said ribbon without completely melting said lead-calcium alloy;
- removing the coated ribbon from said melt;
- cooling the coated ribbon to solidify said coating alloy on said surface;
- and
- expanding the coated ribbon into a grid-forming strip comprising a network of grid wires and nodes interconnecting adjacent said grid wires.
A method of extending the high temperature cycle life of a lead-acid storage battery having a positive electrode comprising a leady active material embedding a current collecting grid comprising a lead-calcium alloy, comprising the steps of:
- rolling a grid substrate material comprising an alloy of lead, calcium and tin to form a wrought ribbon of said material;
- immersing said ribbon into a melt of a molten coating alloy selected from the group consisting of lead antimony and lead-silver alloys for a time sufficient (1) to coat said ribbon with said coating alloy, and (2) to fuse said coating alloy to said surface without completely melting said ribbon;
- removing the coated ribbon from said melt;
- cooling the coated ribbon to solidify said coating alloy on said surface;
- and
- expanding said ribbon into a grid-forming strip comprising a network of grid wires and nodes interconnecting adjacent said grid wires whereby said wrought ribbon is metallurgically recrystallized while in said melt to supplement the cycle-life improving benefits of the coating alloy.