Preparation of aqueous compositions based on fluoroelastomers for coatings having a high thickness
AssigneeAusimont S. p. A.
InventorsDaria Lenti, Tiziana Poggio, Luciano Masini
Life of this patent
Estimating the term…
Abstract
Method of preparation of concentrated aqueous compositions based on fluoroelastomers, capable of giving a coating having a high thickness for each passage on the surface to be protected, consisting in the milling of the additives at the powder state directly into the latex of the fluoroelastomer.
Claims15
Process for preparing concentrated and stable aqueous coating compositions based on fluoroelastomer, capable of giving a protective layer having high thickness without the formation of sagging after each application on the surface to be coated, said process comprising:
- dispersing charges and a cross linking agent into a concentrated aqueous latex of fluoroelastomer by milling said components in their original physical form of dry powder or of liquid in said latex with a microball mill, said milling being carried out for such a time that the viscosity of the composition does not start to decrease, said aqueous latex having a fluoroelastomer concentration higher than 50% by weight with respect to the total weight of the latex and being formed of colloidal particles having less than 1 micron size.
Process according to anyone of the claims from 1 or 2, wherein the crosslinking agent is a polyfunctional amine in an amount comprised between 1 and 10% with respect to the dry weight of the fluoroelastomer.
Process according to anyone of the claims from 1 or 2, wherein the crosslinking agent is a polyhydroxylated compound utilized in the presence of an aminophosphine accelerator.
Process according to anyone of the claims from 1 or 2 wherein the charges utilized are selected from the group formed by carbon black, clay, kaolin, silica, mica, talc, pigments or mixtures of these substances, in total amount comprised between 5 and 50% with respect to the dry weight of the fluoroelastomer.
Process according to anyone of the claims from 1 or 2, wherein it is used as charge polytetrafluoroethylene, which is mixed to the fluoroelastomer latex under the form of concentrated latex and in dry amount comprised between 1 and 10% with respect to the dry weight of the fluoroelastomer.
Process according to anyone of the claims from 1 or 2 wherein the aqueous latex of fluoroelastomer comes from the concentration of the dispersion obtained in the polymerization process, said concentration comprising:
- (i) addition of a non-ionic surface active agent to the aqueous dispersion of the fluoroelastomer;
- (II) heating the dispersion to the temperature corrsponding to the surface active agent clouding;
- (iii) keeping the dispersion at said temperature for about one hour;
- (iv) decantation and separation of the concentrated phase below.
Coating compositions obtained by a process according to anyone of the claims from 1 or 2.
Dependencies are inferred from the claim text.