Paper making process
AssigneeTim-Bar Corporation
InventorCharles W. Propst, Jr.
Life of this patent
Estimating the term…
Abstract
A process for the manufacture of a paper having improved grease and water resistance, yet facilitating recycling of the paper is achieved by applying a recyclable plastic coating to a paper making machine.
Claims17
In a process for making paper wherein a furnish is deposited on a wire and dewatered, the improvement comprising:
- adding to the furnish an effective amount of a repulpable acrylic resin-containing composition wherein the acrylic resin-containing composition is at a pH of at least 5.5 and further comprises zinc oxide in an amount effective to crosslink the acrylic resin.
In a process for making paper, wherein a furnish is deposited on a wire and dewatered to form a paper, and the dewatered paper is subsequently pressed a number of times to further reduce the water content of the paper, the improvement comprising adding an effective amount of a repulpable acrylic resin-containing composition at a pH of at least 5.5, said acrylic resin-containing composition including zinc oxide in an amount effective to crosslink the acrylic resin, to at least one side of the dewatered paper subsequent to a first pressing step.
In a process for making paper wherein a furnish is deposited on a wire and dewatered to form a paper, the dewatered paper is subsequently pressed to further reduce the water content of the paper and is subsequently calendered, the improvement comprising introducing to at least one side of the paper an effective amount of a repulpable acrylic resin-containing composition at a pH of at least 5.5, said acrylic resin-containing composition including zinc oxide in an amount effective to crosslink the acrylic resin, between the pressing and calendering steps.
A process for making paper comprising the following steps:
- (A) applying a furnish to a wire;
- (B) dewatering the furnish and obtaining a water containing paper;
- (C) pressing the water containing paper to reduce the water content;
- (D) calendering the pressed paper;
- (E) recovering a finished paper;
- and
- (F) adding an effective amount of a repulpable acrylic resin-containing composition containing zinc oxide in an amount effective to crosslink the acrylic resin, said resin composition having a pH of at least about 5.5, at any point during said paper making process.
In a process for making paper wherein a furnish is deposited on a wire and dewatered, the improvement comprising adding to the furnish an effective amount of a repulpable acrylic based resin composition wherein the acrylic based resin composition consists of the following components:
- (A) 15 parts by weight of an aqueous acrylic resin emulsion having 34.0.+-.0.5% non-volatiles, a pH of 8.3-8.6, a viscosity (Brookfield) of 2500.+-.500 cps, a density of 1.07, an acid number of 70, a T.sub.g of 95.degree. C. and a flashpoint of 115.degree. C.;
- (B) 65 parts by weight of an aqueous acrylic resin emulsion having 40% non-volatiles, a pH of 2.5-3.5, a viscosity of 25-35 cps, a weight per gallon of 8.7 pounds, an M.F.T. of 8.degree. C., a T.sub.g of 0.degree. C. and an acid number of 58 (@ 100% non-volatiles);
- (C) 6 parts by weight of an aqueous polyethylene was emulsion having 34.7-35.3% non-volatiles, a pH of 9.0-9.5 and a weight per gallon of 8.27 pounds;
- (D) 5.5 parts by weight HOH;
- (E) 0.5 parts by weight NH.sub.4 OH;
- and
- (F) 3 parts by weight zinc oxide solution.
In a process for making paper wherein a furnish is deposited on a wire and dewatered to form a paper, and the dewatered paper is subsequently pressed a number of times to further reduce the water content of the paper, the improvement comprising adding an effective amount of a repulpable acrylic based resin composition to at least one side of the dewatered paper subsequent to a first pressing step wherein the acrylic based resin composition consists of the following components:
- (A) 15 parts by weight of an aqueous acrylic resin emulsion having 34.0.+-.0.5% non-volatiles, a pH of 8.3-8.6, a viscosity (Brookfield) of 2500.+-.500 cps, a density of 1.07, an acid number of 70, a T.sub.g of 95.degree. C. and a flashpoint of 115.degree. C.
- (B) 65 parts by weight of an aqueous acrylic resin emulsion having 40% non-volatiles, a pH of 2.5-3.5, a viscosity of 25-35 cps, a weight per gallon of 8.7 pounds, an M.F.T. of 8.degree. C., a T.sub.g of 0.degree. C. and an acid number of 58 (@ 100% non-volatiles);
- (C) 6 parts by weight of an aqueous polyethylene wax emulsion having 34.7-35.3% non-volatiles, a pH of 9.0-9.5 and a weight per gallon of 8.27 pounds;
- (D) 5.5 parts by weight HOH;
- (E) 0.5 parts by weight NH.sub.4 OH;
- and
- (F) 3 parts by weight zinc oxide solution.
In a process for making paper wherein a furnish is deposited on a wire and dewatered, the dewatered paper is subsequently pressed to further reduce the water content of the paper and subsequently calendered,
- the improvement comprising introducing to at least one side of the paper an effective amount of a repulpable acrylic resin based composition between the pressing and calendering steps wherein the acrylic based resin composition consists of the following components:
- (A) 15 parts by weight of an aqueous acrylic resin emulsion having 34.0.+-.0.5% non-volatile, a pH of 8.3-8.6, a viscosity (Brookfield) of 2500.+-.500 cps, a density of 1.07, an acid number of 70, a T.sub.g of 95.degree. C. and a flashpoint of 115.degree. C.;
- (B) 65 parts by weight of an aqueous acrylic resin emulsion having 40% non-volatiles, a pH of 2.5-3.5, a viscosity of 25-35 cps, a weight per gallon of 8.7 pounds, an M.F.T. of 8.degree. C., a T.sub.g of 0.degree. C. and an acid number of 58 (@ 100% non-volatiles);
- (C) 6 parts by weight of an aqueous polyethylene wax emulsion having 34.7-35.3% non-volatiles, a pH of 9.0-9.5 and a weight per gallon of 8.27 pounds;
- (D) 5.5 parts by weight HOH;
- (E) 0.5 parts by weight NH.sub.4 OH;
- and
- (F) 3 parts by weight zinc oxide solution.
Dependencies are inferred from the claim text.