Manufacture of fluoride glass fibers with phosphate coatings
AssigneeLucent Technologies Inc.
InventorsNonna Kopylov, Ahmet Refik Kortan
Life of this patent
Estimating the term…
Abstract
The specification describes a method for the manufacture of fluoride glass optical fibers which are covered with a protective coating of phosphate glass. The coating is produced by dipping the fluoride glass preform in a phosphate glass melt prior to drawing the optical fiber. The fluoride glass is ZBLAN. The phosphate glass has a glass transition temperature below 200.degree. C., which allows the dipping step to be carried out at a relatively low temperature where the preform temperature is maintained well below the crystallization temperature of the fluoride glass, and also where the viscosity of the fluoride glass preform is substantially higher than the viscosity of the phosphate glass coating material.
Claims9
A method comprising the steps of drawing an optical fiber from a glass preform, and coating the drawn fiber with an optical fiber coating, wherein the improvement comprises overcladding the glass preform with a phosphate glass having a glass transition temperature below 200.degree. C. and at least 30.degree. C. below the glass transition temperature of said glass preform by dipping said glass preform into a phosphate glass melt, the phosphate glass melt having a temperature at which the viscosity of the phosphate glass in the phosphate glass melt is less than the viscosity of the glass in the glass preform.
A method for the manufacture of fluoride glass optical fibers comprising the following steps:
- a. preparing a fluoride glass preform comprising the following composition:
- 50-60% of a fluoride selected from the group consisting of zirconium fluoride, hafnium fluoride and mixtures thereof
- 10-25% barium fluoride
- 3-7% lanthanum fluoride
- 2-5% aluminum fluoride and
- 5-25% sodium fluoride
- b. preparing a phosphate glass melt comprising:
- 60-70% H.sub.3 PO.sub.4,
- 8-30% PbO,
- 6-30% of an oxide selected from the group consisting of Na.sub.2 O, K.sub.2 O and mixtures thereof,
- 0.5-3.0% MgO,
- 0.5-3.0% BaO,
- 0.5-3.0% V.sub.2 O.sub.5 and,
- 0-3.0% CaO
- c. heating the phosphate glass melt to a temperature in the range 300.degree.-350.degree. C.
- d. heating the preform to a temperature in the range 215.degree.-255.degree. C.,
- e. dipping the heated fluoride glass preform into the phosphate glass melt to overclad the fluoride glass preform with a coating of the phosphate glass, and
- f. drawing the preform into a fiber.
A method comprising dipping an optical fiber preform with a first glass composition into glass melt of a second glass composition said melt having a temperature at which the viscosity of the first glass composition is at least 1.5 times the viscosity of the second glass composition, and the glass transition temperature of said second glass composition is below 200.degree. C. and at least 60.degree. C. below the glass transition temperature of said first glass composition, thereby producing a clad optical fiber preform, drawing a glass optical fiber from said clad optical fiber preform, and coating said optical fiber with an optical fiber polymer coating.
Dependencies are inferred from the claim text.