Back to results
US 5,856,406 AGranted
Impact modification of thermoplastics
AssigneeThe Dow Chemical Company
InventorsH. Craig Silvis, Daniel J. Murray, Thomas R. Fiske, Stephen R. Betso, Robert R. Turley
Life of this patent
Estimating the term…
Abstract
Compositions having good low temperature impact performance made from a thermoplastic (e.g., a polyolefin such as polypropylene) and either at least one linear ethylene/C.sub.5 -C.sub.20 .alpha.-olefin or at least one substantially linear ethylene/C.sub.3 -C.sub.20 .alpha.-olefin polymer are disclosed. The compositions are easily molded and have particular utility in making automotive facia, parts and other household articles.
Claims24
A thermoplastic olefinic polymer composition comprising:
- A) polypropylene, and
- B) at least one substantially linear ethylene/.alpha.-olefin interpolymer, wherein the substantially linear ethylene/.alpha.-olefin interpolymer is characterized as having:
- a) a melt flow ratio, I.sub.10 /I.sub.2, .gtoreq.5.63,
- b) a molecular weight distribution, M.sub.w /M.sub.n, defined by the equation:
- M.sub.w /M.sub.n .ltoreq.(I.sub.10 /I.sub.2)--4.63, and
- c) a critical shear rate at onset of surface melt fracture of at least 50 percent greater than the critical shear rate at the onset of surface melt fracture of a linear ethylene/.alpha.-olefin interpolymer having about the same I.sub.2 and M.sub.w /M.sub.n,
- wherein the thermoplastic olefinic polymer composition is characterized as having a notched Izod which is greater than that of a comparative composition which comprises said polypropylene and a linear olefin polymer having the same I.sub.2 and M.sub.w /M.sub.n of said substantially linear ethylene/.alpha.-olefin interpolymer, with the ratio of polypropylene:linear olefin polymer in the comparative composition being the same as the ratio of polmpropylene:substantially linear polymer of the thermoplastic olefinic polymer composition.
4 more elements
A thermoplastic olefinic polymer composition comprising:
- A) polypropylene, and
- B) at least one substantially linear ethylene/.alpha.-olefin interpolymer, wherein the substantially linear ethylene/.alpha.-olefin interpolymer is characterized as having:
- a) a melt flow ratio, I.sub.10 /I.sub.2, .gtoreq.5.63,
- b) a molecular weight distribution, M.sub.w /M.sub.n, defined by the equation:
- M.sub.w /M.sub.n .ltoreq.(I.sub.10 /I.sub.2)--4.63, and
- c) a processing index less than or equal to about 70% of the PI of a linear ethylene/.alpha.-olefin interpolymer having about the same I.sub.2 and M.sub.w /M.sub.n,
- wherein the thermoplastic olefinic polymer composition is characterized as having a notched Izod which is greater than that of a comparative composition which comprises said polypropylene and a linear olefin polymer having the same I.sub.2 and M.sub.w /M.sub.n of said substantially linear ethylene/.alpha.-olefin interpolymer, with the ratio of polypropylene:linear olefin polymer in the comparative composition being the same as the ratio of polypropylene:substantially linear polymer of the thermoplastic olefinic polymer composition.
4 more elements
A thermoplastic olefinic polymer composition comprising:
- A) polypropylene, and
- B) at least one substantially linear ethylene/.alpha.-olefin interpolymer characterized as having:
- a) a melt flow ratio, I.sub.10 /I.sub.2, .gtoreq.5.63,
- b) a molecular weight distribution, M.sub.w /M.sub.n, defined by the equation:
- M.sub.w /M.sub.n .ltoreq.(I.sub.10 /I.sub.2)--4.63, and
- c) a critical shear rate at onset of surface melt fracture of at least 50 percent greater than the critical shear rate at the onset of surface melt fracture of a linear ethylene/.alpha.-olefin interpolymer having about the same I.sub.2 and M.sub.w /M.sub.n,
- wherein the thermoplastic olefinic polymer composition is characterized as having a Dynatup energy value at -20.degree. F. which is greater than that of a comparative composition which comprises said polypropylene and a linear olefin polymer having the same .sub.2 and M.sub.w /M.sub.n of said substantially linear ethylene/.alpha.-olefin interpolymer, with the ratio of polypropylene:linear olefin polymer in the comparative composition being the same as the ratio of polypropylene:substantially linear polymer of the thermoplastic olefinic polymer composition.
4 more elements
A thermoplastic olefinic polymer composition having good low temperature impact performance comprising:
- A) polypropylene, and
- B) at least one linear ethylene/.alpha.-olefin, interpolymer having a density of about 0.865 to about 0.89 g/cm.sup.3, a short chain branching distribution (SCBDI) of greater than about 50, and wherein the .alpha.-olefin is a C.sub.5 -C.sub.20 .alpha.-olefin, and wherein the thermoplastic olefinic polymer composition is characterized as having a Dynatup energy value at -20.degree. F. which is greater than that of a comparative composition which comprises said polypropylene and a linear olefin polymer having the same I.sub.2 and M.sub.w /M.sub.n of said substantially linear ethylene/.alpha.-olefin interpolymer, with the ratio of polypropylene:linear olefin polymer in the comparative composition being the same as the ratio of polypropylene:substantially linear polymer of the thermoplastic olefinic polymer composition.
A thermoplastic olefinic polymer composition comprising:
- A) polypropylene, and
- B) at least one substantially linear ethylene/.alpha.-olefin interpolymer characterized as having:
- a) a melt flow ratio, I.sub.10 /I.sub.2, .gtoreq.5.63,
- b) a molecular weight distribution, M.sub.w /M.sub.n, defined by the equation:
- M.sub.w /M.sub.n .ltoreq.(I.sub.10 /I.sub.2)--4.63, and
- c) a processing index less than or equal to about 70% of the PI of a linear ethylene/.alpha.-olefin interpolymer having about the same I.sub.2 and M.sub.w /M.sub.n,
- wherein the thermoplastic olefinic polymer composition is characterized as having a Dynatup energy value at -20.degree. F. which is greater than that of a comparative composition which comprises said polypropylene and a linear olefin polymer having the same I.sub.2, and M.sub.w /M.sub.n of said substantially linear ethylene/.alpha.-olefin interpolymer, with the ratio of polypropylene:linear olefin polymer in the comparative composition being the same as the ratio of polypropylene:substantially linear polymer of the thermoplastic olefinic polymer composition.
4 more elements
A thermoplastic olefinic polymer composition having a Dynatup Energy at -20.degree. F. of at least about 30 foot-pounds impact performance comprising:
- A) polypropylene, and
- B) at least one substantially linear ethylene/.alpha.-olefin interpolymer characterized as having:
- a) a melt flow ratio, I.sub.10 /I.sub.2, which is at least about 7, and
- b) a molecular weight distribution, M.sub.w /M.sub.n, from about 1.5 to about 2.5, and
- c) a density of from about 0.865 to about 0.89 g/cm.sup.3,
- wherein the thermoplastic olefin polymer composition is formed into an injection molded, blow molded, or profile extruded part.
3 more elements
A thermoplastic olefinic polymer composition having a Dynatup Energy at -20.degree. F. of at least about 30 foot-pounds impact performance comprising:
- A) polypropylene, and
- B) at least one linear ethylene/C.sub.5 -C.sub.20 .alpha.-olefin interpolymer having a density of from about 0.865 g/cm.sup.3 to about 0.89 g/cm.sup.3, a short chain branching distribution (SCBDI) of greater than about 50, and wherein the thermoplastic olefin polymer composition is formed into an injection molded, blow molded, or profile extruded part.
A thermoplastic olefinic polymer composition having a Dynatup Energy at -20.degree. F. of at least about 30 foot-pounds impact performance comprising:
- A) polypropylene, and
- B) about 30 percent by weight of at least one substantially linear ethylene/.alpha.-olefin interpolymer characterized as having:
- a) a melt flow ratio, I.sub.10 /I.sub.2, .gtoreq.5.63,
- b) a molecular weight distribution, M.sub.w /M.sub.n, defined by the equation:
- M.sub.w /M.sub.n .ltoreq.(I.sub.10 /I.sub.2)--4.63, and
- c) a critical shear rate at onset of surface melt fracture of at least 50 percent greater than the critical shear rate at the onset of surface melt fracture of a linear ethylene/.alpha.-olefin interpolymer having about the same 12 and M.sub.w /M.sub.n.
3 more elements
A thermoplastic olefinic polymer composition having a Dynatup Energy at -20.degree. F. of at least about 30 foot-pounds impact performance comprising:
- A) polypropylene, and
- B) about 30 percent by weight of at least one substantially linear ethylene/.alpha.-olefin interpolymer characterized as having:
- a) a melt flow ratio, I.sub.10 /I.sub.2, .gtoreq.5.63,
- b) a molecular weight distribution, M.sub.w /M.sub.n, defined by the equation:
- M.sub.w /M.sub.n .ltoreq.(I.sub.10 /I.sub.2)--4.63, and
- c) a processing index less than or equal to about 70% of the PI of a linear ethylene/.alpha.-olefin interpolymer having about the same I.sub.2 and M.sub.w /M.sub.n.
3 more elements
A thermoplastic olefinic polymer composition having a Dynatup Energy at -20.degree. F. of at least about 30 foot-pounds impact performance comprising:
- A) polypropylene, and
- B) about 30 percent by weight at least one linear ethylene/.alpha.-olefin interpolymer, wherein the .alpha.-olefin is a C.sub.5 -C.sub.20 .alpha.-olefin, and wherein the interpolymer has a density of from about 0.865 g/cm.sup.3 to about 0.89 g/cm.sup.3, a short chain branching distribution (SCBDI) of greater than about 50, and wherein the thermoplastic olefin polymer composition is formed into an injection molded, blow molded, or profile extruded part.
Dependencies are inferred from the claim text.