Back bedding sealant composition
AssigneeSchnee-Morehead, Inc.
InventorsHun R. Choung, Edward T. Clutter, Aureliano Perez
Life of this patent
Estimating the term…
Abstract
A water borne back bedding sealant formulated from an acrylic polymer emulsion and a urethane polymer emulsion provides superior adhesion, tensile properties, low temperature flexibility, rheology and bond strength. In one embodiment of the present invention, the back bedding sealant comprises the following components: from 50% to 75% by weight of an acrylic polymer emulsion, from 7% to 25% by weight of a urethane polymer emulsion which is compatible with the acrylic polymer emulsion plus minor amounts of components to be selected from a list comprising: rheology modifiers, glycols, mineral oil, silanes, Ph adjusters, surfactants, water, silicas, and antimicrobial agents. These superior properties can be attained even with a clear sealant.
Claims13
A sealant composition comprising:
- a back bedding sealant formed from a blend of
- from 50% to 75% by weight of an acrylic polymer emulsion;
- and
- from 7% to 25% by weight of a urethane polymer emulsion;
- the sealant composition having an ultimate tensile strength of at least 90 psi when cured at a temperature less than 85.degree. F. and wherein said back bedding sealant may be flexibly elongated at least 100% after curing.
A sealant composition comprising:
- A back bedding sealant formed from a blend of
- from 50% to 75% by weight of an acrylic polymer emulsion;
- from 7% to 25% by weight of a urethane polymer emulsion;
- and
- from about 0.1% to about 8.0% of additives to be selected from the group consisting of:
- rheology modifiers, glycols, mineral oil, silanes, hydroxides and amines, surfactants, water, silicas, and antimicrobial agents.
- the sealant composition having an ultimate tensile strength of at least 90 psi when cured at a temperature less than 85.degree. F. and wherein said back bedding sealant may be elongated at least 100% after curing.
A sealant composition comprising:
- a back bedding sealant formed from a blend of
- from 50% to 75% by weight of an acrylic polymer emulsion;
- from 7% to 25% by weight of a urethane polymer emulsion, said urethane polymer emulsion being compatible with said acrylic polymer emulsion;
- from about 0.1% to about 8.0% additives to be selected from the group consisting of:
- rheology modifiers, glycols, mineral oil, silanes, hydroxides and amines, surfactants, water, silicas, and antimicrobial agents;
- said back bedding sealant having a tensile strength of at least 30 psi at 25% elongation and an ultimate tensile strength of at least 90 psi when cured at a temperature less than 85.degree. F. and wherein the back bedding sealant may be elongated at least 100% after curing.
A sealant composition comprising:
- a back bedding sealant formed from a blend of
- from 50% to 75% by weight of an acrylic polymer emulsion;
- from 7% to 25% by weight of a urethane polymer emulsion, said urethane polymer emulsion being compatible with said acrylic polymer emulsion;
- and
- from about 0.1% to about 8% additives to be selected from the group consisting of:
- rheology modifiers, glycols, mineral oil, silanes, hydroxides and amines, surfactants, water, silicas, and antimicrobial agents;
- and
- said composition having a tensile strength of at least 30 psi at 25% elongation, an ultimate tensile strength of at least 90 psi at a temperature less than 85.degree. F. and lap shear strength of at least 100 psi between glass and wood substrates after three weeks curing time at ambient (less than 85.degree. F.) temperature and wherein said back bedding sealant may be elongated at least 100% after curing.
Dependencies are inferred from the claim text.