Method of reinforcing molded body of ceramic and reinforced mold body of ceramic
AssigneeHonda Giken Kogyo Kabushiki Kaisha
InventorsYoshikatsu Higuchi, Masanori Okabe, Yasunobu Kawakami
Life of this patent
Estimating the term…
Abstract
A reinforced molded body of ceramic, which is to be fired, is produced by adding ceramic fibers to a matrix of ceramic. The ceramic fibers are composed of silicon, nitrogen, oxygen, and carbon, the carbon and the oxygen having a total content of at most 10 weight % and having respective contents at a ratio ranging from 0.08 to 2.
Claims10
A method of manufacturing a sintered ceramic molded body from a molded ceramic body prepared by slip casting, said method comprising the steps of:
- adding 0.62 to 9.3 weight % of ceramic fibers produced from polysilazane to a ceramic matrix of silicon nitride, wherein said ceramic fibers consist essentially of silicon, nitrogen, oxygen, and carbon, and have a length ranging from 10 to 1000 .mu.m, wherein said carbon and said oxygen have a total content of at most 10 weight % based on the ceramic fibers and wherein the ratio of the weight of the carbon to the weight of the oxygen ranges from 0.08 to 2, in order to increase the strength of the molded ceramic body and maintain the strength of said sintered ceramic molded body produced therefrom;
- molding the ceramic matrix with the added ceramic fibers, as a slurry having a concentration ranging from 40 to 60 volume %, into said molded ceramic body according to slip casting;
- and
- firing the molded ceramic body to produce said sintered ceramic molded body.
A sintered ceramic molded body that is suitable for being manufactured from a molded ceramic body prepared by slip casting, said sintered ceramic molded body comprising:
- a ceramic matrix of silicon nitride;
- and
- 0.62 to 9.3 weight % of ceramic fibers produced from polysilazane and added to said ceramic matrix, wherein said ceramic fibers consist essentially of silicon, nitrogen, oxygen, and carbon, and have a length ranging from 10 to 1000 .mu.m, wherein said carbon and said oxygen have a total content of at most 10 weight % based on the ceramic fibers and wherein the ratio of the weight of the carbon to the weight of the oxygen ranges from 0.08 to 2, so that the strength of the molded ceramic body can be increased and the strength of said sintered ceramic molded body produced therefrom can be maintained, and said ceramic matrix and said ceramic fibers being molded from a slurry having a concentration ranging from 40 to 60 volume %.
Dependencies are inferred from the claim text.