Polyolefin elastomer composition
AssigneeToyoda Gosei Co., Ltd.
InventorsJunji Koizumi, Haruyasu Mizutani, Yoshiaki Shichida
Life of this patent
Estimating the term…
Abstract
A composition for making an elongated molded product which can be satisfactorily used without having to be painted. The composition comprises an elastomer comprising crystalline polypropylene and ethylene-.alpha.-olefin rubber (EOR), and 0 to 15 phr of talc. The polypropylene (PP) and EOR have a blending ratio (PP/EOR) by weight of 35/65 to 67/33. The polypropylene has a Q value (M.sub.w /M.sub.n).gtoreq.10 and a melt flow rate of 50 to 120. The EOR has an .alpha.-olefin content of 10 to 20% by weight. The proportion Y of talc and the proportion X of the EOR in the elastomer satisfy the relation: Y.gtoreq.-0.63X+34.
Claims18
A composition comprising the following ingredients:
- (a) a crystalline polypropylene having an M.sub.w /M.sub.n value Q.gtoreq.10 and a melt flow rate between 50 and 120,
- (b) an ethylene-.alpha.-olefin rubber having an .alpha.-olefin content between 10 wt. % and 20 wt. %, wherein the amounts by weight of said crystalline polypropylene and said ethylene-.alpha.-olefin rubber are characterized by a blending ratio with respect to each other between 35/65 and 67/33,
- (c) 0-15 phr (parts per hundred weight of rubber) talc, wherein the amount phr by weight of said talc is with respect to the sum of the amounts of said crystalline polypropylene and said ethylene-.alpha.-olefin rubber, and
- the phr amount by weight of said talc, Y, and the amount by weight of said ethylene-.alpha.-olefin rubber in said blending ratio, X, is characterized by:
- Y.gtoreq.-0.63X+34
- wherein 0.ltoreq.Y.ltoreq.15.
A composition comprising the following ingredients:
- (a) a crystalline polypropylene which forms a hard-phase in said composition and has an M.sub.w /M.sub.n value Q.gtoreq.10 and a melt flow rate between 50 and 120,
- (b) an ethylene propylene rubber having a Mooney viscosity between 3 and 35 ML.sub.1+4 at 100.degree. C., and
- (c) an ethylene-.alpha.-olefin rubber containing a C.sub.4 -C.sub.12 .alpha.-olefin and having a specific gravity of at most 0.892, said ethylene propylene rubber and said ethylene-.alpha.-olefin rubber forming a soft-phase in said composition and characterized by a blending ratio by weight between 1/9 and 9/1,
- wherein said hard-phase of crystalline polypropylene and said soft-phase of ethylene propylene rubber and ethylene-.alpha.-olefin rubber are characterized by a blending ratio by weight between 48/52 and 67/33.
A composition comprising the following ingredients:
- (a) a crystalline polypropylene copolymer forming a hard-phase in said composition and having an M.sub.w /M.sub.n value Q.gtoreq.10, having a melt flow rate between 50 and 120, and containing between 2 and 12 wt. % copolymerized ethylene,
- (b) an ethylene propylene rubber having a Mooney viscosity between 3 and 35 ML.sub.1+4 at 100.degree. C. and a propylene content between 20 and 45 wt. %, and
- (c) an ethylene-.alpha.-olefin rubber containing a C.sub.4 -C.sub.12 .alpha.-olefin content between 10 and 22 wt. %, and having a specific gravity between 0.870 and 0.892, said ethylene propylene rubber and said ethylene-.alpha.-olefin rubber forming a soft-phase in said composition and characterized by a blending ratio by weight between 1/9 and 9/1,
- wherein said hard-phase of crystalline polypropylene copolymer and said soft-phase of ethylene propylene rubber and ethylene-.alpha.-olefin rubber are characterized by a blending ratio between 48/52 and 67/33.