Patching composition for concrete surfaces
OwnerHarold Donaldsoninventor
Life of this patent
Estimating the term…
Abstract
A patching composition in the form of a putty composition for application to concrete surfaces. The composition comprises a substantial portion of a conventional cement, such as a Portland cement, and a silica sand selected to have the right consistency and density along with calcium oxide. The composition is then mixed in water and applied to voids or holes in a concrete wall. The composition, when applied as a single coating and fully cured, results in an appearance similar to that of the concrete and provides strength characteristics substantially equivalent to that of the original concrete.
Claims19
A light weight patching composition for a single coat application to rough surfaced concrete surfaces having holes and voids with a coating thickness and which patching composition has substantially less weight than a conventional concrete to which the patchy composition is applied and which can also match the surface appearance of the original concrete surface and provide a smooth unmottled surface thereto, said composition comprising:
- a) a cementitious material in an amount of about 25% to about 65% by weight based on the total weight of the composition;
- b) a silica sand having a particle size within the range of No. 30 to No. 60 sieve sizes and which has a size selected so that the patching composition can readily fill a selected void or hole, the silica sand being present in an amount of about 25% by weight to about 65% by weight based on the total weight of the composition;
- c) a calcium oxide mixture containing at least 90% calcium oxide and present in an amount effective to increase the curing rate of the composition and the degree of bonding, said amount of calcium oxide being greater than the amount of calcium oxide found in a cementitious composition formulated with a Portland cement and at least about 4% by weight to about 30% by weight based on the total weight of the composition;
- and
- d) the patching composition being mixed with water and having a viscosity with a thick consistency sufficient to create a putty to fill in voids or holes in a concrete surface and remain therein during a hardening stage and also provides a smooth surface texture, said composition being formulated so that it can be applied in a single coat application to provide said smooth unmottled surface, with a coating thickness of no less than about 1/8 inch and no greater than about 1/4 inch, and which composition has an initial cure time of up to about 30 minutes, said composition also having a surface appearance and texture similar to the concrete surface to which the composition is applied.
A patching composition for a single coat application to rough surfaced concrete surfaces having holes and voids with a selected coating thickness and which patching composition has substantially less weight than conventional concrete to which the patching composition is applied and which can also match the surface appearance of the original concrete surface and provide a smooth unmottled surface thereto, said composition comprising:
- a) a cementitious material in an amount of about 25% to about 65% by weight based on the total weight of the composition;
- b) a first silica sand having roughly about a No. 30 sieve size and which has a sieve size selected so that the patching composition can readily fill selected voids and holes, the silica sand being present in an amount of about 12% to about 25% by weight based on the total weight of the composition;
- c) a second silica sand having a particle size of roughly about No. sieve size 60 and which is present in an amount of about 25% to about 45% by weight based on the weight of the composition;
- d) a calcium oxide mixture containing at least 90% calcium oxide and present in an amount effective to increase the curing rate of the composition and the degree of bonding, said amount of calcium oxide being greater than the amount of calcium oxide found in a cementitious composition formulated with a Portland cement and at least about 4% by weight to about 30% by weight based on the total weight of the composition;
- and
- e) the patching composition being mixed with water and having a viscosity with a thick consistency sufficient to create a putty to fill in voids or holes in a concrete surface and remain therein during a hardening stage and also provides a smooth surface texture, said composition being formulated so that it can be applied in a single coating application to provide said smooth unmottled surface, with a coating thickness of no less than about 1/8 inch and no greater than about 1/4 inch, and which composition has an initial cure time of up to about 30 minutes, said composition also having a surface appearance and texture similar to the concrete surface to which the composition is applied.
A method for patching holes and voids in rough surface textured concrete surfaces in a single coat composition and which is made from a concrete composition comprising a Portland cement by using and applying in a single coating an improved light weight patching composition which also matches the surface appearance of the original concrete surface, said method comprising applying to the voids and holes a patching composition comprised of:
- a) a cementitious material in an amount of about 25% to about 65% by weight based on the total weight of the composition;
- b) a silica sand having a particle sieve size which is selected so that the patching composition will readily fill a selected void or hole, the silica sand being present in an amount of about 15% by weight to about 65% by weight based on the total weight of the composition;
- c) a calcium oxide mixture containing at least 90% calcium oxide and having a high calcium content present in an amount which is substantially greater than the amount of calcium oxide found in the concrete to which the patching composition is applied and which calcium oxide is present in an amount of at least about 4% by weight to about 30% by weight based on the total weight of the patching composition;
- and
- d) the patching composition being mixed with water and having a viscosity with a thick consistency sufficient to create a putty to fill in voids or holes in a concrete surface and remain therein during a hardening stage and also provide a smooth surface texture, said composition being formulated so that it can be applied in a single coating application to provide a smooth unmottled surface, with a coating thickness of no less than about 1/8 inch and no more than about 1/4 inch, and which composition has an initial cure time of up to about 30 minutes, said composition also having a surface appearance and texture similar to the concrete surface to which the composition is applied.
Dependencies are inferred from the claim text.