Supported catalyst and process for catalytic oxidation of volatile organic compounds

A method for making a catalyst useful for effective catalytic oxidative destruction of volatile organic compounds, comprising the steps of:

• (a) providing an aqueous solution of chromium nitrate, adding the solution to a porous support material having surface area of 10-400 m.sup.2 /g, then drying and calcining the metal loaded support material;
• (b) mixing ammonium platinum nitrate aqueous solution with an alcohol carrier liquid;
• (c) contacting the metal loaded support material with the platinum nitrate solution so as to form clusters and limit diffusion of the platinum solution into the porous support material, and restrict the platinum to only a thin outer layer on the support material, and evaporating the carrier liquid;
• (d) reducing the metal loaded support material with a hydrogen-containing gas and converting the platinum oxide to its metal state;
• and
• (e) calcining the metal loaded support material in air so as to produce the active oxidative catalyst.

A method for making a catalyst useful for effective catalytic oxidative destruction of volatile organic compounds, comprising the steps of:

• (a) providing an aqueous solution of chromium nitrate, adding the chromium nitrate solution to particles of a porous alumina support material having surface area of 10-400 m.sup.2 /g, and then drying and calcining the metal-loaded support material particles at temperature exceeding 50.degree. C.;
• (b) mixing ammonium platinum nitrate aqueous solution with isopropanol carrier liquid;
• (c) contacting the metal loaded support material particles and the platinum nitrate solution for a time sufficient to form clusters and provide only limited diffusion of the platinum solution into the porous support material, and thereby restrict the platinum to only a thin outer layer on the support material, then evaporating the alcohol fraction carrier liquid and water at 80.degree.-110.degree. C. temperature;
• (d) reducing the metal loaded support material particles in a hydrogen-nitrogen gas mixture at 100.degree.-800.degree. C. and converting the platinum to its metal state;
• and
• (e) calcining the metal loaded support material particles in air at 200.degree.-700.degree. C. so as to provide the active oxidative catalyst.

A process for catalytically oxidizing volatile organic compounds (VOCs) having a concentration of between about 1 ppm and 5 vol % in an oxygen-containing gas which is free of any catalyst poisoning material, the process comprising:

• providing a feedstream containing dilute concentration of at least one volatile organic compound in gaseous form and contacting the feedstream under reaction conditions with a catalyst containing:
• an inert porous support material having total surface area of 10-400 m.sup.2 /g, a transition metal oxide selected from the group consisting of chromium, cobalt and copper provided on the porous support material in concentration of 0.5-15 wt. % of the catalyst;
• and
• an active noble metal consisting of platinum having concentration of 0.010-2.0 wt. % of the catalyst in a thin outer layer having thickness not exceeding about 0.10 mm and in interaction with the transition metal oxide, wherein at least the active noble metal exists in the thin layer on only the outer surface of the support material so as to minimize mass transfer resistance from reactant compounds and provide high catalytic activity while also minimizing the weight percent of the active metal in the catalyst, the feedstream contacting the catalyst under reaction conditions of 50.degree.-500.degree. C. temperature, 0-600 psig pressure, and space velocity of 1000-200,000 hr.sup.-1 ;
• and
• oxidizing the volatile organic compounds contained in the feedstream to yield essentially only carbon dioxide and water products.

A process for catalytically oxidizing volatile organic compounds (VOCs) having a concentration of between about 1 ppm and 5 vol% in an oxygen-containing gas which is free of any catalyst poisoning material, the process comprising:

• (a) providing a feedstream containing dilute concentrations of volatile organic compounds in gaseous form, and contacting the feedstream selected from the group consisting of acetates, alcohols, alkanes, alkenes, aldehydes, aromatics, carboxylic acids, ketones, halogenated hydrocarbons and mixtures thereof under reaction conditions with a catalyst containing:
• an inert porous support material having total surface area of 50-300 m.sup.2 /g, a transition metal provided on the porous support material in concentration of 1-10 wt. % of the catalyst;
• an active noble metal having concentration of 0.012-1.0 wt. % of the catalyst in a thin outer layer having thickness not exceeding about 0.10 mm and in combination with the transition metal wherein at least the active noble metal exists in the thin layer on only the outer surface of the support material so as to minimize mass transfer resistance from reactant compounds and provide high catalytic activity while also minimizing the weight percent of the active metal in the catalyst,
• (b) contacting the catalyst with the feedstream under reaction conditions of 100.degree.-400.degree. C. temperature, 0-100 psig pressure, and space velocity of 3000-100,000 hr.sup.1 ;
• and
• (c) oxidizing the volatile organic compounds contained in the feedstream to yield essentially carbon dioxide and water products.