Process for formation of epitaxial film
AssigneeCanon Kabushiki Kaisha
InventorsTakeshi Ichikawa, Hidemasa Mizutani
Life of this patent
Estimating the term…
Abstract
A process for forming an epitaxial film on a biased substrate by sputtering a target to which a bias voltage and a plasma-generating high-frequency power are applied, wherein the film formation is carried out in an atmosphere having H.sub.2 O, CO and CO.sub.2 partial pressures controlled at 1.0.times.10.sup.-8 Torr, with the substrate temperature maintained in the range of from 400.degree. to 700.degree. C. The epitaxial film obtained by the process has excellent interface characteristics, very low impurity contents, good crystallinity and excellent step coverage, and is suitable for application to semiconductor devices.
Claims7
A process for forming a silicon-containing epitaxial film on a substrate arranged in a film-forming space by a sputtering method comprising the steps of:
- (a) introducing into said film-forming space containing said substrate therein a plasma-generating raw process gas containing 1 ppm or less of each of H.sub.2 O, CO and CO.sub.2 ;
- (b) controlling the partial pressure of each of said H.sub.2 O, CO and CO.sub.2 to a value of 1.0.times.10.sup.-8 Torr or less and the sum of the partial pressures of said H.sub.2 O, CO and CO.sub.2 to a value of 1.0.times.10.sup.-8 Torr or less in the gaseous atmosphere in said film-forming space;
- (c) maintaining said substrate at a temperature in the range of 400.degree. to 700.degree. C.;
- (d) applying a DC voltage to a silicon-containing target arranged in said film-forming space while simultaneously applying a plasma-generating high frequency power to said silicon containing target, to produce plasma in said film forming space, wherein said silicon-containing target is sputtered by said plasma to cause the formation of said silicon-containing epitaxial film on said substrate.
A process for forming a silicon-containing epitaxial film on a substrate arranged in a film-forming space by a sputtering method said process comprising the steps of:
- (a) introducing into said film-forming space containing said substrate therein a plasma-generating process gas containing 1 ppm or less of each of H.sub.2 O, CO and CO.sub.2 ;
- (b) controlling the partial pressure of each of said H.sub.2 O, CO and CO.sub.2 to a value of 1.0.times.10.sup.-8 Torr or less and the sum of the partial pressures of said H.sub.2 O, CO and CO.sub.2 to a value of 1.0.times.10.sup.-8 Torr or less in the gaseous atmosphere in said film-forming space;
- (c) maintaining said substrate at a temperature in the range of 400.degree. to 700.degree. C.;
- (d) applying a DC voltage to a silicon-containing target arranged in said film-forming space while simultaneously applying a plasma-generating high frequency power to said silicon-containing target and a high frequency power of a frequency higher than that of said plasma-generating high frequency power to said substrate, to produce plasma in said film-forming space, wherein said silicon-containing target is sputtered by said plasma to cause the formation of said silicon-containing epitaxial film on said substrate.
A process for forming a silicon-containing epitaxial film on a substrate arranged in a film-forming space by a sputtering method, said process comprising the steps of:
- (a) introducing a plasma-generating raw process gas whose content of each of H.sub.2 O, CO, and CO.sub.2 being 1 ppm or less into said film-forming space containing said substrate therein;
- (b) controlling the gaseous atmosphere in said film-forming space to have a vacuum, wherein a partial pressure of each of said H.sub.2 O, CO, and CO.sub.2 is 1.0.times.10.sup.-8 or less, and the sum of the partial pressures of said H.sub.2 O, CO, and CO.sub.2 is 1.0.times.10.sup.-8 or less;
- (c) maintaining said substrate at a temperature in the range of 400.degree. to 700.degree. C.;
- and
- (d) applying a DC voltage to a silicon-containing target arranged in said film-forming space while simultaneously applying a plasma-generating high frequency power to said silicon-containing target to produce plasma in said film-forming space, wherein said silicon-containing target is sputtered by said plasma to cause the formation of said silicon-containing epitaxial film on said substrate.
Dependencies are inferred from the claim text.