Process for cleaning metal machine parts caked with thermoplastic polymer
AssigneeMovengineering S.r.l.
InventorMario Mignani
Life of this patent
Estimating the term…
Abstract
Process for cleaning metal machine parts caked with thermoplastic polymers and apparatus for carrying out said process. The process consists in placing the parts caked with polymers inside an autoclave and in striking them with a stream of overheated steam. The stream mixes with the vaporized polymer residues produced by the thermal decomposition and hydrolysis of the polymers that are initially present on the parts and is conveyed outside the autoclave together with the vaporized residues. The stream containing vaporized polymer residues that leaves the autoclave is then subjected to condensation and the pollutants elimination.
Claims12
Process for cleaning metal machine parts caked with thermoplastic polymers, comprising the following steps:
- 1A-placing the parts caked with polymer inside an autoclave heated at a temperature of 380.degree.-450.degree. C. and closing the autoclave;
- 1B-fluxing the autoclave with a stream of overheated steam to quickly eliminate every trace of air from the autoclave, thereby an environment void of oxygen is obtained in the autoclave;
- 1C-feeding in said autoclave a stream of superheated steam at a temperature of 400.degree.-500.degree. C. to simultaneously subject the polymer to hydrolysis and pyrolysis in the absence of oxygen, thereby oxidation, molecular chain reticulation phenomena and formation of carbonious residues are prevented and all the polymer is vaporized, thereby vaporized polymer residues are formed without leaving any solid or liquid waste in the autoclave, the temperature of the superheated steam being about 20.degree.-50.degree. C. higher than the temperature of the autoclave walls, in order to avoid decrease of the temperature inside the autoclave below the temperature of the autoclave walls during the progressive breakage of the polymer molecular chains, because of an endothermic effect of the hydrolysis reaction, said vaporized polymer residues leaving the autoclave in a stream containing said vaporized polymer residues and superheated steam, said feeding being continued until all the polymer degradable by hydrolysis is degraded.